Vapor deposition of molybdenum oxide using bis(ethylbenzene) molybdenum and water
Three molybdenum precursors—bis(acetylacetonate) dioxomolybdenum, molybdenum isopropoxide, and bis(ethylbenzene) molybdenum—were tested for molybdenum oxide vapor deposition. Quartz crystal microbalance studies were performed to monitor growth. Molybdenum isopropoxide and bis(ethylbenzene) molybdenum achieved linear growth rates 0.01 and 0.08 Å/cycle, respectively, using atomic layer deposition techniques. Negligible MoO{sub x} growth was observed on alumina powder using molybdenum isopropoxide, as determined by inductively coupled plasma optical emission spectroscopy. Bis(ethylbenzene) molybdenum achieved loadings of 0.5, 1.1, and 1.9 Mo/nm{sup 2} on alumina powder after one, two, and five cycles, respectively, using atomic layer deposition techniques. The growth window for bis(ethylbenzene) molybdenum is 135–150 °C. An alternative pulsing strategy was also developed for bis(ethylbenzene) molybdenum that results in higher growth rates in less time compared to atomic layer deposition techniques. The outlined process serves as a methodology for depositing molybdenum oxide for catalytic applications. All as-deposited materials undergo further calcination prior to characterization and testing.
- OSTI ID:
- 22592843
- Journal Information:
- Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films, Vol. 34, Issue 5; Other Information: (c) 2016 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA); ISSN 0734-2101
- Country of Publication:
- United States
- Language:
- English
Similar Records
Atomic layer deposition of molybdenum oxide using bis(tert-butylimido)bis(dimethylamido) molybdenum
Nucleation and growth of molybdenum disulfide grown by thermal atomic layer deposition on metal oxides