Influence of Sm doping on structural and dielectric properties of Y{sub 1-x}Sm{sub x}MnO{sub 3} (x = 0, 0.10, 0.20) manganites
- School of Physics, Vigyan Bhawan, Devi Ahilya University, Khandwa Road Campus, Indore 452001 (India)
Structural and dielectric properties of polycrystalline YMnO{sub 3} (x = 0.0, 0.10 and 0.20) which was prepared by solid-state reaction route, have been investigated. The X-ray diffraction pattern reveals that all the samples are in single phase and show hexagonal structure with P63cm space group. The particle size decreases with increase in Sm doping while to that X-ray density increases with increasing x. The dielectric constant (ε’) of Y{sub 1-x}Sm{sub x}MnO{sub 3} measured in the frequency range 10 Hz to 1MHz is much higher at lower frequencies (≤ 1KHz) and its value decreases with enhanced frequency. At very high frequencies, ε’ becomes frequency independent and is attributed to Maxwell Wagner type of interfacial polarization model. A very high value of dielectric constant ∼18642 is observed for x = 10%. The dielectric loss (tan δ) decreases wit increase in Sm doping.
- OSTI ID:
- 22591367
- Journal Information:
- AIP Conference Proceedings, Vol. 1728, Issue 1; Conference: ICC 2015: International conference on condensed matter and applied physics, Bikaner (India), 30-31 Oct 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Temperature dependence anomalous dielectric relaxation in Co doped ZnO nanoparticles
Room temperature multiferroic properties and magnetoelectric coupling in Sm and Ni substituted Bi{sub 4−x}Sm{sub x}Ti{sub 3−x}Ni{sub x}O{sub 12±δ} (x = 0, 0.02, 0.05, 0.07) ceramics
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
71 CLASSICAL AND QUANTUM MECHANICS
GENERAL PHYSICS
CONCENTRATION RATIO
DIELECTRIC MATERIALS
FREQUENCY DEPENDENCE
HEXAGONAL LATTICES
MANGANATES
MHZ RANGE
PARTICLE SIZE
PERMITTIVITY
POLARIZATION
POLYCRYSTALS
SAMARIUM COMPOUNDS
SPACE GROUPS
X-RAY DIFFRACTION
YTTRIUM COMPOUNDS