MnFe{sub 2}O{sub 4} as a gas sensor towards SO{sub 2} and NO{sub 2} gases
- Department of Natural Sciences, NIIT University, Neemrana, Rajasthan 301705 (India)
The chemical co-precipitation method was used to synthesize MnFe{sub 2}O{sub 4} nanoparticles. Single cubic phase formation of nanoparticles was confirmed by X-ray diffraction technique. The average particle size of MnFe{sub 2}O{sub 4} nanoparticles was found to be 10.7 nm using Scherrer formula. The ultrafine powder of MnFe{sub 2}O{sub 4} nanoparticles was pressed to design pellet of 10 mm diameter and 1mm thickness. Copper electrodes have been deposited on the surface of pellet using silver paste in the form of capacitor. Fabricated gas sensing device of MnFe{sub 2}O{sub 4} nanoparticles was tested towards SO{sub 2} and NO{sub 2} gases. Cole-Cole plot of MnFe{sub 2}O{sub 4} was investigated with the help of electrochemical workstation. The performance of the sensors including sensitivity, response and recovery time was also determined. It was observed that the MnFe{sub 2}O{sub 4} nanoparticles are more sensible for NO{sub 2} gas as compared to SO{sub 2} gas.
- OSTI ID:
- 22591321
- Journal Information:
- AIP Conference Proceedings, Vol. 1728, Issue 1; Conference: ICC 2015: International conference on condensed matter and applied physics, Bikaner (India), 30-31 Oct 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Complex Electric Modulus Spectroscopy of (MnFe{sub 2}O{sub 4}){sub x}/CuTl-1223 Nanoparticles-Superconductor Composites
Reverse micelle synthesis and characterization of superparamagnetic MnFe{sub 2}O{sub 4} spinel ferrite nanocrystallites