Interfacial reactions and wetting in Al-Mg sintered by powder metallurgy process
- Physics Department, Math and Science Faculty, Institute of Technology Sepuluh Nopember (ITS) Jl. Arief Rahman Hakim, Surabaya 60111 (Indonesia)
Was conducted to analyze the effect of temperature variation on the bonding interface sintered composite Al-Mg and analyze the effect of variations of the density and hardness sinter. Research carried out by the base material powders of Al, Mg powder and solvent n-butanol. The method used in this study is a powder metallurgy, with a composition of 60% volume fraction of Al - 40% Mg. Al-Mg mixing with n-butanol for 1 hour at 500 rpm. Then the emphasis (cold comression) with a size of 1.4 cm in diameter dies and height of 2.8 cm, is pressed with a force of 20 MPa and held for 15 minutes. After the sample into pellets, then sintered at various temperatures 300 °C, 350 °C, 400 °C and 450 °C. Characterization is done by using the testing green density, sintered density, X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), vickers microhardness, and press test. XRD data analysis done by using X’Pert High Score Plus (HSP) to determine whether there is a new phase is formed. Test results show that the sintered density increasing sintering temperature, the resulting density is also increasing (shrinkage). However, at a temperature of 450 °C decreased (swelling). With the increased sinter density, interfacial bonding getting Kuta and more compact so that its hardness is also increased. From the test results of SEM / EDX, there Mg into Al in the border area. At temperatures of 300 °C, 350 °C, 400 °C, the phase formed is Al, Mg and MgO. While phase is formed at a temperature of 450 °C is aluminum magnesium (Al{sub 3}Mg{sub 2}), Aluminum Magnesium Zinc (AlMg{sub 2}Zn).
- OSTI ID:
- 22591132
- Journal Information:
- AIP Conference Proceedings, Vol. 1725, Issue 1; Conference: ICAMST 2015: 3. international conference on advanced materials science and technology, Semarang (Indonesia), 6-7 Oct 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
An investigation of wear behaviors of different Monel alloys produced by powder metallurgy
High-Throughput Combinatorial Development of High-Entropy Alloys For Light-Weight Structural Applications
Related Subjects
ALUMINIUM
ALUMINIUM ALLOYS
BONDING
BUTANOLS
COMPOSITE MATERIALS
DENSITY
INTERFACES
MAGNESIUM
MAGNESIUM ALLOYS
MAGNESIUM OXIDES
MICROHARDNESS
POWDER METALLURGY
PRESSURE RANGE MEGA PA
SCANNING ELECTRON MICROSCOPY
SINTERING
TEMPERATURE DEPENDENCE
VICKERS HARDNESS
X-RAY DIFFRACTION
ZINC ALLOYS