Structural characterization and electrical conductivity of the Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} solid series
Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} (x=0, 0.1, 0.2, 0.4, 0.6, 0.8, 0.99) is prepared by using a solid reaction route, and single phase is achieved. Structural and phase transformation of Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} have been characterized by high temperature X-ray diffraction. The lattice parameters a, b, c decrease and γ increases with increasing x, at both room and high temperature. The phase transformation temperature increases linearly with increasing x for Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ}. The electrical conductivity of Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} is measured in wet air. A clear relationship between the structural, phase transformation and electrical conductivity of Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} is built, which will provide a guideline to tailor the electrical conductivity. - Graphical abstract: Structural and phase transformation of Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} have been characterized by high temperature X-ray diffraction, as well as the conductivity of Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} in wet air. A clear relationship between the structural, phase transformation and electrical conductivity of Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} is built. - Highlights: • Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} with various Sm contents was prepared. • Structure, phase transformation and electrical conductivity of Ca{sub 0.01}La{sub 0.99−x}Sm{sub x}NbO{sub 4−δ} were characterized. • A relationship between the structure, phase transformation and electrical conductivity was well established.
- OSTI ID:
- 22584077
- Journal Information:
- Journal of Solid State Chemistry, Vol. 237; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Assessment of co-sintering as a fabrication approach for metal-supported proton-conducting solid oxide cells
Anisotropic hyperfine field fluctuation in La{sub 0.67}Ca{sub 0.33}Mn{sub 0.99}Fe{sub 0.01}O{sub 3}