Effect of cation distribution on the magnetic and hyperfine behaviour of nanocrystalline Co doped Ni–Zn ferrite (Ni{sub 0.4}Zn{sub 0.4}Co{sub 0.2}Fe{sub 2}O{sub 4})
- Solid State Research Laboratory, Department of Physics, Burdwan University, Burdwan 713104 (India)
- UGC-DAE Consortium for Scientific Research, III/LB-8, Kolkata 700098 (India)
Highlights: • Cation distribution in tetrahedral and octahedral sites of spinel Ni{sub 0.4}Zn{sub 0.4}Co{sub 0.2}Fe{sub 2}O{sub 4}. • Structural analysis of observed X-ray diffraction pattern using Rietveld method. • Study of hyperfine behaviour using Mössbauer spectroscopy. • Static and dynamic magnetic measurements. • Correlation of cation distributions obtained from Rietveld analysis with the results of magnetic and Mössbauer effect measurements. - Abstract: Nanoparticles of Ni{sub 0.4}Zn{sub 0.4}Co{sub 0.2}Fe{sub 2}O{sub 4} are prepared by a simple co-precipitation method. The as dried sample is heat treated at 400, 500, 600, 700 and 800 °C to obtain different sizes of nanoparticles. The crystallographic phase of the samples is confirmed analyzing observed X-ray diffraction (XRD) by Rietveld method. Hyperfine parameters of the samples are derived from room temperature (RT) Mössbauer spectra of the samples. Magnetic properties of the samples are investigated by static and dynamic hysteresis loops. Different magneto-crystalline parameters are calculated from the variation of magnetization with temperature (M–T curve) under zero field cooled (ZFC) and field cooled (FC) conditions of the as dried sample. The cation distribution estimated from Rietveld analysis are correlated with the results of magnetic and Mössbauer effect measurements. The observed high value of saturation magnetization (72.7 emu/g at RT) of the sample annealed at 800 °C would be interesting for applications in different electromagnetic devices.
- OSTI ID:
- 22581515
- Journal Information:
- Materials Research Bulletin, Vol. 76; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Enhanced magnetic behavior, exchange bias effect, and dielectric property of BiFeO{sub 3} incorporated in (BiFeO{sub 3}){sub 0.50} (Co{sub 0.4}Zn{sub 0.4}Cu{sub 0.2} Fe{sub 2}O{sub 4}){sub 0.5} nanocomposite
Investigation of structural and magnetic properties of Ni{sub 0.5}Zn{sub 0.5}Fe{sub 2}O{sub 4} nano powders prepared by self combustion method
Related Subjects
77 NANOSCIENCE AND NANOTECHNOLOGY
ABSORPTION SPECTRA
ABSORPTION SPECTROSCOPY
ANNEALING
CATIONS
COBALT COMPOUNDS
COPRECIPITATION
CRYSTAL STRUCTURE
CRYSTALS
DOPED MATERIALS
FERRATES
MAGNETIC PROPERTIES
MAGNETIZATION
NANOPARTICLES
NANOSTRUCTURES
NICKEL COMPOUNDS
TEMPERATURE DEPENDENCE
TEMPERATURE RANGE 0273-0400 K
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION
ZINC COMPOUNDS