Correlation among far-infrared reflection modes, crystal structures and dielectric properties of Ba(Zn{sub 1/3}Nb{sub 2/3})O{sub 3}–CaTiO{sub 3} ceramics

Journal Article · Tue Mar 15 00:00:00 EDT 2016 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2015.11.036· OSTI ID:22581467

Shi, Feng; Sun, Haiqing; Liu, Hongquan; Xu, Guogang; Wang, Jing; Han, Ye

Highlights: • Crystal symmetry decreases with CT concentration from cubic to hexagonal structure. • Lattice constants as well as the ordered degree change with CT concentration. • Ordered structures turn from 1:1 to 1:2 ordering with change of crystal structures. • There is a correlation between FIR phonon modes and dielectric properties. • There is a correlation between FIR phonon modes and crystal structures. - Abstract: Ba(Zn{sub 1/3}Nb{sub 2/3})O{sub 3} (BZN)–CaTiO{sub 3} (CT) microwave dielectric ceramics were synthesized at 1395 °C for 4 h using conventional solid-state sintering technique with different CT contents. The ceramics were characterized by X-ray diffraction (XRD) and far-infrared reflection (FIR) spectroscopy to evaluate correlations among crystal structures, dielectric properties, and infrared modes. XRD results showed that crystal symmetry decreased with increased CT concentration from cubic to hexagonal structure, and lattice constants and ordered degree changed accordingly. Ordered phases transformed from 1:1 to 1:2 ordered structure with crystal-structure change. FIR results demonstrated that two new IR active modes appeared at 300 cm{sup −1}, and another new mode appeared at 600 cm{sup −1} for the x ≥ 0.60 sample, which agreed with the change in crystal structures as confirmed by XRD results. Correlations between FIR modes and dielectric properties were established.

• OSTI ID: 22581467
• Journal Information: Materials Research Bulletin, Vol. 75; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ABSORPTION SPECTROSCOPY
BARIUM COMPOUNDS
CALCIUM COMPOUNDS
CERAMICS
COMPUTERIZED TOMOGRAPHY
CONCENTRATION RATIO
CORRELATIONS
CRYSTAL STRUCTURE
CRYSTALS
DIELECTRIC MATERIALS
DIELECTRIC PROPERTIES
INFRARED SPECTRA
LATTICE PARAMETERS
MICROWAVE RADIATION
NIOBATES
PHONONS
SINTERING
TITANATES
X-RAY DIFFRACTION
ZINC OXIDES