Crystal structures of the new ternary stannides La{sub 3}Mg{sub 4−x}Sn{sub 2+x} and LaMg{sub 3−x}Sn{sub 2}
- Università degli Studi di Genova, Dipartimento di Chimica e Chimica Industriale, via Dodecaneso 31, 16146 Genova (Italy)
- Università degli Studi di Milano, Dipartimento di Chimica, Via Golgi 19, 20133 Milano (Italy)
Synthesis and structural characterization of the two new lanthanum–magnesium–stannides La{sub 3}Mg{sub 4−x}Sn{sub 2+x} (0.12≤x≤0.40) and LaMg{sub 3−x}Sn{sub 2} (0.33≤x≤0.78) are reported. The crystal structures of these intermetallics were determined by single crystal X-ray diffraction analysis and confirmed by Rietveld refinement of powder X-ray diffraction patterns of the corresponding samples. The La{sub 3}Mg{sub 4−x}Sn{sub 2+x} phase crystallizes in the hexagonal Zr{sub 3}Cu{sub 4}Si{sub 2} structure type (P6¯2m, hP9, Z=3, x=0.12(1), a=7.7974(7), c=4.8384(4) Å), which represents an ordered derivative of the hP9-ZrNiAl prototype, ubiquitous among equiatomic intermetallics. The LaMg{sub 3–x}Sn{sub 2} phase is the second representative of the trigonal LaMg{sub 3−x}Ge{sub 2} type, which is a superstructure of the LaLi{sub 3}Sb{sub 2} structure type (P3¯1c, hP34-0.12, Z=6, x=0.35(1), a=8.3222(9), c=14.9546(16) Å). The scheme describing the symmetry reduction/coloring with respect to the parent type is reported here with the purpose to discuss the LaMg{sub 3−x}Sn{sub 2} off-stoichiometry from the geometrical point of view. Structural relationships between the La–Mg–Sn ternary phases, including the already known equiatomic LaMgSn compound (oP12-TiNiSi), are presented in the framework of the AlB{sub 2}-related compounds family and discussed with the aid of group-subgroup relations in the Bärnighausen formalism. - Graphical abstract: Crystal structure of LaMg{sub 3−x}Sn{sub 2} viewed along the (001) direction together with the puckered layer of Mg and Sn atoms hosting Mg2, Mg3 and vacancy □. - Highlights: • Crystal structures of the new La{sub 3}Mg{sub 4−x}Sn{sub 2+x} and LaMg{sub 3−x}Sn{sub 2} phases were determined. • The off-stoichiometry of LaMg{sub 3−x}Sn{sub 2} was discussed from geometrical point of view. • Structural relations between the known La–Mg–Sn phases were established. • The studied compounds are related to the AlB{sub 2} type by symmetry reduction.
- OSTI ID:
- 22577757
- Journal Information:
- Journal of Solid State Chemistry, Vol. 233; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
A phase width for CaGaSn. Crystal structure of mixed intermetallic Ca{sub 4}Ga{sub 4+x}Sn{sub 4−x} and SmGa{sub x}Sn{sub 3−x}, stability, geometry and electronic structure
K{sub 2}Mg{sub 5-x}Sn{sub 3} and K{sub 3}Mg{sub 18}Tt{sub 11} (Tt=Sn, pb) with two types of Mg-Sn/Pb frameworks