Magnetic properties of CaCu{sub 5}-type RNi{sub 3}TSi (R=Gd and Tb, T=Mn, Fe, Co and Cu) compounds
- Department of Chemistry, Moscow State University, Leninskie Gory, House 1, Building 3, GSP-2, Moscow 119992 (Russian Federation)
- Department of Petrology, Geological Faculty, Moscow State University, Leninskie Gory, Moscow 119992 (Russian Federation)
- Research Center for Solid State Physics and Materials, School of Mathematics and Physics, Suzhou University of Science and Technology, Suzhou 215009 (China)
- Department of Chemistry and Chemical Biology, McMaster University, 1280 Main Street West, Hamilton, Ontario, Canada L8S 4M1 (Canada)
- Indian Institute of Technology Madras, Chennai 600036 (India)
- Departamento de Física Teórica e Experimental, Universidade Federal do Rio Grande do Norte, Natal 59082-970 (Brazil)
Magnetic properties and magnetocaloric effect of CaCu{sub 5}-type RNi{sub 3}TSi (R=Gd and Tb, T=Mn, Fe, Co and Cu) compounds have been investigated. Magnetic measurements of RNi{sub 3}TSi display the increasing of Curie temperature and the decreasing of magnetocaloric effect and saturated magnetic moment in the row of ‘RNi{sub 3}CuSi–RNi{sub 3}NiSi–RNi{sub 3}CoSi–RNi{sub 3}MnSi–RNi{sub 3}FeSi’. In contrast to GdNi{sub 3}{Mn, Fe, Co}Si, TbNi{sub 3}{Mn, Fe, Co}Si exhibit significant magnetic hysteresis. The coercive field increases from TbNi{sub 4}Si (~0.5 kOe) to TbNi{sub 3}CoSi (4 kOe), TbNi{sub 3}MnSi (13 kOe) and TbNi{sub 3}FeSi (16 kOe) in field of 50 kOe at 5 K, whereas TbNi{sub 3}CuSi exhibits a negligible coercive field. - Graphical abstract: Magnetic measurements of RNi{sub 3}TSi show the increasing of Curie temperature and the decreasing of magnetocaloric effect and saturated magnetic moment in the row of 'RNi{sub 3}CuSi–RNi{sub 3}NiSi–RNi{sub 3}CoSi–RNi{sub 3}MnSi–RNi{sub 3}FeSi'. In contrast to GdNi{sub 3}{Mn, Fe, Co}Si, TbNi{sub 3}{Mn, Fe, Co}Si exhibit significant magnetic hysteresis. The coercive field increases from TbNi{sub 4}Si (~0.5 kOe) to TbNi{sub 3}CoSi (4 kOe), TbNi{sub 3}MnSi (13 kOe) and TbNi{sub 3}FeSi (16 kOe) in field of 50 kOe at 5 K, whereas TbNi{sub 3}CuSi exhibits a negligible coercive field. - Highlights: • CaCu{sub 5}-type RNi{sub 3}TSi show ferromagnetic ordering (R=Gd, Tb, T=Mn–Co, Cu). • Curie point increases in ‘RNi{sub 3}CuSi–RNi{sub 3}NiSi–RNi{sub 3}CoSi–RNi{sub 3}MnSi–RNi{sub 3}FeSi’ row. • MCE decreases in ‘RNi{sub 3}CuSi–RNi{sub 3}NiSi–RNi{sub 3}CoSi–RNi{sub 3}MnSi–RNi{sub 3}FeSi’ row. • TbNi{sub 3}{Mn, Fe, Co}Si exhibit significant magnetic hysteresis. • The coercive field of TbNi{sub 3}MnSi and TbNi{sub 3}FeSi reach 13 kOe and 16 kOe at 5 K.
- OSTI ID:
- 22573974
- Journal Information:
- Journal of Solid State Chemistry, Vol. 232; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English