Morphology and conductivity study of solid electrolyte Li{sub 3}PO{sub 4}
- Engineering Physics, Sepuluh Nopember Institute of Technology ITS Campus, Sukolilo, Surabaya 6011 (Indonesia)
- Center for Science and Technology of Advanced Materials, National Nuclear Energy Agency Kawasan Puspiptek Serpong, Tangerang Selatan15314, Banten (Indonesia)
The comparison between two different methods of synthesize of solid electrolyte Li{sub 3}PO{sub 4} as precursor material for developing lithium ion battery, has been performed. The first method is to synthesize Li{sub 3}PO{sub 4} prepared by wet chemical reaction from LiOH and H{sub 3}PO{sub 4} which provide facile, abundant available resource, low cost, and low toxicity. The second method is solid state reaction prepared by Li{sub 2}CO{sub 3} and NH{sub 4}H{sub 2}PO{sub 4.} In addition, the possible morphology identification of comparison between two different methods will also be discussed. The composition, morphology, and additional identification phase and another compound of Li{sub 3}PO{sub 4} powder products from two different reaction are characterized by SEM, EDS, and EIS. The Li{sub 3}PO{sub 4} powder produced from wet reaction and solid state reaction have an average diameter of 0.834 – 7.81 µm and 2.15 – 17.3 µm, respectively. The density of Li{sub 3}PO{sub 4} prepared by wet chemical reaction is 2.238 gr/cm{sup 3}, little bit lower than the sample prepared by solid state reaction which density is 2.3560 gr/cm{sup 3}. The EIS measurement result shows that the conductivity of Li{sub 3}PO{sub 4} is 1.7 x 10{sup −9} S.cm{sup −1} for wet chemical reaction and 1.8 x 10{sup −10} S.cm{sup −1} for solid state reaction. The conductivity of Li{sub 3}PO{sub 4} is not quite different between those two samples even though they were prepared by different method of synthesize.
- OSTI ID:
- 22494623
- Journal Information:
- AIP Conference Proceedings, Vol. 1710, Issue 1; Conference: NNS2015: 6. nanoscience and nanotechnology symposium, Surakarta (Indonesia), 4-5 Nov 2015; Other Information: (c) 2016 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Syntheses, properties and applications of framework titanium phosphates with open structures
Solid electrolyte for solid-state batteries: Have lithium-ion batteries reached their technical limit?