Effects of catalyst support and chemical vapor deposition condition on synthesis of multi-walled carbon nanocoils
- Department of Electrical and Electronic Information Engineering, Toyohashi University of Technology, Toyohashi, Aichi 441-8580 (Japan)
- Fuji Research Laboratory, Tokai Carbon Co., Ltd., Oyama, Shizuoka 410-1431 (Japan)
- Toho Gas Co., Ltd., Tokai, Aichi 476-8501 (Japan)
Multi-walled carbon nanocoil (MWCNC) is a carbon nanotube (CNT) with helical shape. We have synthesized MWCNCs and MWCNTs hybrid by chemical vapor deposition (CVD). MWCNCs are considered to be a potential material in nanodevices, such as electromagnetic wave absorbers and field emitters. It is very important to take into account the purity of MWCNCs. In this study, we aimed to improve the composition ratio of MWCNCs to MWCNTs by changing catalyst preparation and CVD conditions. As a catalyst, Fe{sub 2}O{sub 3}/zeolite was prepared by dissolving Fe{sub 2}O{sub 3} fine powder and Y-type zeolite (catalyst support material) in ethanol with an Fe density of 0.5wt.% and with a zeolite density of 3.5wt.%. The catalyst-coated Si substrate was transferred immediately onto a hotplate and was heated at 80°C for 5 min. Similarly, Fe{sub 2}O{sub 3}/Al{sub 2}O{sub 3}, Co/zeolite/Al{sub 2}O{sub 3}, Co/zeolite, and Co/Al{sub 2}O{sub 3} were prepared. The effect of the difference of the composite catalysts on synthesis of MWCNCs was considered. The CVD reactor was heated in a tubular furnace to 660-790°C in a nitrogen atmosphere at a flow rate of 1000 ml/min. Subsequently, acetylene was mixed with nitrogen at a flow rate ratio of C{sub 2}H{sub 2}/N{sub 2} = 0.02-0.1. The reaction was kept under these conditions for 10 min. MWCNTs and MWCNCs were well grown by the catalysts of Co/zeolite and Co/Al{sub 2}O{sub 3}. The composition ratio of MWCNCs to MWCNTs was increased by using a combination of zeolite and Al{sub 2}O{sub 3}. The highest composition ratio of MWCNCs to MWCNTs was 12%.
- OSTI ID:
- 22494583
- Journal Information:
- AIP Conference Proceedings, Vol. 1709, Issue 1; Conference: IRAGO conference 2015: 360 degree outlook on critical scientific and technological challenges for a sustainable society, Aichi (Japan), 22-23 Oct 2015; Other Information: (c) 2016 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Carbon Nanotube Formation on Cr-Doped Ferrite Catalyst during Water Gas Shift Membrane Reaction: Mechanistic Implications and Extended Studies on Dry Gas Conversions
X-ray photoelectron spectroscopy study on Fe and Co catalysts during the first stages of ethanol chemical vapor deposition for single-walled carbon nanotube growth