Strain softening mechanism at meso scale during micro-compression in an ultrafine-grained pure copper
- Key Laboratory of Micro-systems and Micro-structures Manufacturing of Ministry of Education, Harbin Institute of Technology, Harbin, 150080 (China)
Strain softening behavior has been found at meso scale using micro-compression testing in an ultrafine-grained (UFG) pure copper by comparison with the typical strain hardening in conventional coarse-grained (CG) material. Microstructural observations show that grain size remains nearly the same including the fraction of high-angle grain boundaries during micro-compression in UFG pure copper. The Kernel average misorientation(KAM) distribution measured by electron backscatter diffraction (EBSD), as a statistical method, is applied to qualitatively evaluate dislocation density in the interior of the grains. It is suggested that the deformation mechanisms are dominated by grain boundary sliding and grain rotation accompanied by dislocation slip in UFG pure copper, which demonstrates that the strain softening behavior is primarily caused by dislocation annihilation during micro-compression.
- OSTI ID:
- 22492356
- Journal Information:
- AIP Advances, Journal Name: AIP Advances Journal Issue: 9 Vol. 5; ISSN AAIDBI; ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ultrafine gradient microstructure induced by severe plastic deformation under sliding contact conditions in copper
Ensembles of gliding grain boundary dislocations in ultrafine grained materials produced by severe plastic deformation