Rietveld refinement and dielectric properties of (Na{sub 0.5}Bi{sub 0.5}TiO{sub 3})-(Bi{sub 0.8}Ba{sub 0.2}FeO{sub 3}) ceramics
- Department of Applied Physics, Guru Jambheshwar University of Science and Technology, Hisar-125001 (India)
(1-x)(Na{sub 0.5}Bi{sub 0.5}TiO{sub 3})-x(Bi{sub 0.8}Ba{sub 0.2}FeO{sub 3}) lead free ceramics (NBT, NBT-BBFO; x = 0.0, 0.1 respectively) have been synthesized by conventional solid state reaction method. Crystalline phase of sintered ceramics was investigated at room temperature using X-ray diffraction. Rietveld refinement of XRD data performed by FullProf revealed that both the samples exhibited rhombohedral structure with R3c space group. Dielectric properties of these ceramics were studied at different temperatures in a wide frequency range using impedance analyzer. Dielectric constant and dielectric loss were found to be increase with increase of BBFO content. The prepared ceramics exhibit a broad maximum in dielectric permittivity at 593K and dispersive permittivity at high temperatures. The NBT-BBFO sample shows a relaxor ferroelectric behavior at different frequencies.
- OSTI ID:
- 22490600
- Journal Information:
- AIP Conference Proceedings, Vol. 1665, Issue 1; Conference: 59. DAE solid state physics symposium 2014, Tamilnadu (India), 16-20 Dec 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Rietveld refinement and dielectric studies of Bi{sub 0.8}Ba{sub 0.2}Fe{sub 0.95}V{sub 0.05}O{sub 3} ceramic
Synthesis and characterization of lead-free 0.5Ba(Zr{sub 0.2}Ti{sub 0.8})O{sub 3}-0.5(Ba{sub 0.7}Ca{sub 0.3})TiO{sub 3} ceramic