Size dependence of magnetorheological properties of cobalt ferrite ferrofluid
Journal Article
·
· AIP Conference Proceedings
Cobalt Ferrite nanoparticles were synthesized using co-precipitation method at reaction temperatures of 40°C and 80°C. X-Ray diffraction studies confirm cubic phase formation. The average crystallite sizes were found to be ∼30nm and ∼48nm for 40°C sample and 80°C sample respectively. Magnetic properties measured using vibrating sample magnetometer show higher coercivety and magnetization for sample prepared at 80°C. Magnetorheological properties of CoFe2O4 ferrofluids were measured and studied.
- OSTI ID:
- 22490328
- Journal Information:
- AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1665; ISSN 0094-243X; ISSN APCPCS
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of Bi{sup 3+} Substitution on Structural, Morphological, and Magnetic Properties of Cobalt Ferrite Nanoparticles
High-Temperature Ferrofluids Based on Molten Salts
Effect of deposition pressure on the structural and magnetic properties of cobalt ferrite thin films
Journal Article
·
Tue Oct 15 00:00:00 EDT 2019
· Journal of Superconductivity and Novel Magnetism
·
OSTI ID:22919533
High-Temperature Ferrofluids Based on Molten Salts
Journal Article
·
Mon Dec 16 23:00:00 EST 2024
· Industrial & Engineering Chemistry Research
·
OSTI ID:2588257
Effect of deposition pressure on the structural and magnetic properties of cobalt ferrite thin films
Journal Article
·
Mon Jun 03 00:00:00 EDT 2013
· AIP Conference Proceedings
·
OSTI ID:22118527