Ti-Nb thin films deposited by magnetron sputtering on stainless steel
- Department of Materials Engineering, Federal University of Sao Carlos, CEP 13565-905 Sao Carlos, São Paulo (Brazil)
Thin films of Ti-Nb alloys were deposited on AISI 316L stainless steel substrate by magnetron sputtering, and the structure, composition, morphology, and microstructure of the films were analyzed by means of x-ray diffraction (XRD), (scanning) transmission electron microscopy (TEM) coupled with energy-dispersive x-ray spectroscopy, atomic force microscopy (AFM), and x-ray photoelectron spectroscopy (XPS). Thin films of four compositions were produced: Ti{sub 85}Nb{sub 15} (Ti-26 wt. % Nb), Ti{sub 80}Nb{sub 20} (Ti-33 wt. % Nb), Ti{sub 70}Nb{sub 30} (Ti-45 wt. % Nb), and Ti{sub 60}Nb{sub 40} (Ti-56 wt. % Nb). Structural characterization by XRD indicated that only the β phase was present in the thin films and that the increase in the Nb content modified the alloy film texture. These changes in the film texture, also detected by TEM analysis, were attributed to different growth modes related to the Nb content in the alloy films. The mean grain sizes measured by AFM increased with the Nb amount (from 197 to 222 nm). XPS analysis showed a predominance of oxidized Ti and Nb on the film surfaces and an enrichment of Ti.
- OSTI ID:
- 22489805
- Journal Information:
- Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films, Vol. 34, Issue 2; Other Information: (c) 2016 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA); ISSN 0734-2101
- Country of Publication:
- United States
- Language:
- English
Similar Records
Preparation and characterization of RF magnetron sputtered CuO/CaTi{sub 4}O{sub 9} thin films with enhanced third-order nonlinear optical properties
Improvement of adhesion and barrier properties of biomedical stainless steel by deposition of YSZ coatings using RF magnetron sputtering