Trap states in enhancement-mode double heterostructures AlGaN/GaN high electron mobility transistors with different GaN channel layer thicknesses
- Key Laboratory of Wide Band Gap Semiconductor Materials and Devices, School of Microelectronics, Xidian University, Xi'an 710071 (China)
- School of Advanced Materials and Nanotechnology, Xidian University, Xi'an 710071 (China)
This is the report on trap states in enhancement-mode AlGaN/GaN/AlGaN double heterostructures high electron mobility transistors by fluorine plasma treatment with different GaN channel layer thicknesses. Compared with the thick GaN channel layer sample, the thin one has smaller 2DEG concentration, lower electron mobility, lower saturation current, and lower peak transconductance, but it has a higher threshold voltage of 1.2 V. Deep level transient spectroscopy measurements are used to obtain the accurate capture cross section of trap states. By frequency dependent capacitance and conductance measurements, the trap state density of (1.98–2.56) × 10{sup 12 }cm{sup −2} eV{sup −1} is located at E{sub T} in a range of (0.37–0.44) eV in the thin sample, while the trap state density of (2.3–2.92) × 10{sup 12 }cm{sup −2} eV{sup −1} is located at E{sub T} in a range of (0.33–0.38) eV in the thick one. It indicates that the trap states in the thin sample are deeper than those in the thick one.
- OSTI ID:
- 22489099
- Journal Information:
- Applied Physics Letters, Journal Name: Applied Physics Letters Journal Issue: 6 Vol. 107; ISSN APPLAB; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Neutron irradiation effects on electrical properties and deep-level spectra in undoped n-AlGaN/GaN heterostructures
Room-temperature mobility above 2200 cm{sup 2}/V·s of two-dimensional electron gas in a sharp-interface AlGaN/GaN heterostructure