Magnetic and structural properties of yellow europium oxide compound and Eu(OH){sub 3}
- Cavendish Laboratory, University of Cambridge, J. J Thomson Av., Cambridge CB3 0HE (United Kingdom)
- Department of Physics and IPAP, Yonsei University, Seoul 120-749 (Korea, Republic of)
- Laboratorio de Cerámicos y Nanomateriales, Facultad de Ciencias Físicas, Universidad Nacional Mayor de San Marcos, Ap. Postal 14-0149, Lima, Perú (Peru)
A new material based on a yellow europium oxide compound was prepared from europium oxide in a high vacuum environment. The structural and magnetic properties of the material were investigated. Owing to the absence of a crystal structure, the material exhibited a disordered magnetic behavior. In a reaction with deionized (DI) water without applied heat, the compound assumed a white color as soon as the DI water reached the powder, and the structure became polycrystalline Eu(OH){sub 3}. The magnetic properties, such as the thermal hysteresis, disappeared after the reaction with DI water, and the magnetic susceptibility of the yellow oxide compound weakened. The magnetic properties of Eu(OH){sub 3} were also examined. Although Eu{sup 3+} is present in Eu(OH){sub 3}, a high magnetic moment due to the crystal field effect was observed. - Graphical abstract: (top left) Optical image of the yellow europium oxide compound. (top right) Optical image of the product of DI water and yellow europium oxide. (bottom) Magnetization curves as a function of temperature measured in various magnetic field. - Highlights: • We prepared a new material based on a yellow europium oxide compound from europium oxide. • We characterized the magnetic properties of the material which exhibits a disordered magnetic behavior such as thermal hysteresis. • The compound turned white (Eu(OH){sub 3}) as soon as the DI water reached the powder. • The thermal hysteresis disappeared after the reaction with DI water and the magnetic susceptibility of the yellow oxide compound weakened.
- OSTI ID:
- 22486729
- Journal Information:
- Journal of Solid State Chemistry, Vol. 228; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
The effects of re-firing process under oxidizing atmosphere and temperatures on the properties of strontium aluminate phosphors
Neutron powder diffraction and magnetic study of perovskites Pb(Mn{sub 1/2}Nb{sub 1/2})O{sub 3} and Pb(Mn{sub 1/4}Fe{sub 1/4}Nb{sub 1/2})O{sub 3}