Imaging and characterization of γ′ and γ″ nanoparticles in Inconel 718 by EDX elemental mapping and FIB–SEM tomography
Microstructural characterization of Inconel 718 superalloy after three different heat treatment variants was performed by electron microscopy and electron tomography techniques, taking advantage of recent development in quantitative electron microscopy. Distribution maps of the chemical elements, collected by ChemiSTEM™ EDX system, offer a clear contrast between γ′, γ″, and the γ matrix. It was found that the γ′ phase contains mainly Ni, Al, and Ti, while the γ″ phase contains Ni, Nb, and Ti. Thus application of the Al and Nb STEM–EDX elemental maps enables identification and size measurements of γ′ and γ″ nanoparticles. 3D morphology of γ′ and γ″ precipitates was examined by electron microscopy and FIB–SEM tomography. Employed methods revealed that in all three heat treatment variants the γ′ particles are almost spheroidal while the γ″ precipitates are mainly elongated-disc shaped. However, the precipitate sizes differed for each variant contributing to differences in the yield strength. Tomographic images were used for estimation of the volume fraction of the both strengthening phases. - Highlights: • ChemiSTEM™ EDX elemental maps bring a fast mean to differentiate γ′ and γ″ particles. • Such maps enable for the explicit size measurements of γ′ and γ″ nanoparticles. • Explicit γ′ and γ″ phases total volume fraction was measured employing FIB–SEM. • γ′/γ″ co-precipitates and sandwich-like γ′/γ″/γ′ particles were present. • HRSTEM-HAADF imaging revealed atomic columns of the γ′/γ″ co-precipitates.
- OSTI ID:
- 22476033
- Journal Information:
- Materials Characterization, Journal Name: Materials Characterization Vol. 100; ISSN 1044-5803; ISSN MACHEX
- Country of Publication:
- United States
- Language:
- English
Similar Records
Understanding the microstructural stability in a γ'-strengthened Ni-Fe-Cr-Al-Ti alloy