Mesoporous mixed-phase Ga{sub 2}O{sub 3}: Green synthesis and enhanced photocatalytic activity
- School of Resources and Environmental Engineering, Wuhan University of Technology, 122 Luoshi Road, Wuhan 430070 (China)
Highlights: • Mixed-phase Ga{sub 2}O{sub 3} was synthesized by a facile and green method. • Mixed-phase Ga{sub 2}O{sub 3} exhibited good photocatalytic activity and stability. • The reactive species in the photocatalytic process were investigated. - Abstract: Mesoporous mixed-phase Ga{sub 2}O{sub 3} was synthesized by calcining the GaOOH precursor. The composition, crystal phase and microstructures of Ga{sub 2}O{sub 3} were characterized in detail. The phase composition of the as-prepared Ga{sub 2}O{sub 3} depended on the calcination temperature and the mixed-phase Ga{sub 2}O{sub 3} was obtained at 600–700 °C. As compared to the pure-phase α-Ga{sub 2}O{sub 3} and β-Ga{sub 2}O{sub 3}, the mixed-phase Ga{sub 2}O{sub 3} exhibited an enhanced photocatalytic property for the degradation of metronidazole solution. The heterojunction in the mixed-phase Ga{sub 2}O{sub 3} was beneficial to the separation of photogenerated electrons and holes. Moreover, the mixed-phase Ga{sub 2}O{sub 3} possessed mesopore structure, which increased more reaction sites and was in favor of the contact of metronidazole molecules with reaction sites. The recycling experiments show that the mixed-phase Ga{sub 2}O{sub 3} has good stability and can be separated easily from the reaction system.
- OSTI ID:
- 22475852
- Journal Information:
- Materials Research Bulletin, Vol. 68; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Controlled synthesis of mesoporous {alpha}-Fe{sub 2}O{sub 3} nanorods and visible light photocatalytic property
Mesoporous anatase TiO{sub 2}/reduced graphene oxide nanocomposites: A simple template-free synthesis and their high photocatalytic performance