Structural and magnetic study of Al{sup 3+} doped Ni{sub 0.75}Zn{sub 0.25}Fe{sub 2−x}Al{sub x}O{sub 4} nanoferrites
Graphical abstract: Hyperfine field of individual sites (inset) and weighted average hyperfine field as a function of Al{sup 3+} content for Ni{sub 0.75}Zn{sub 0.25}Fe{sub 2−x}Al{sub x}O{sub 4}. - Highlights: • Grain size reduction with Al{sup 3+} substitution. • Preferred occupancy of Al{sup 3+} at B site for higher Al{sup 3+} content. • Reduction in Ms, Tc, and hyperfine field with increasing Al{sup 3+} content. • Size dependent variation in coercivity. • Changes in isomer shift due to competing effect of volume and substitution. - Abstract: Nanostructured Al{sup 3+} doped Ni{sub 0.75}Zn{sub 0.25}Fe{sub 2−x}Al{sub x}O{sub 4} (x = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0) ferrites were synthesized via the wet chemical method. X-ray diffraction, transmission electron microscopy, and magnetization measurements have been used to investigate the structural and magnetic properties of spinel ferrites calcined at 950 °C. With the doping of Al{sup 3+}, the particle size of Ni{sub 0.75}Zn{sub 0.25}Fe{sub 2−x}Al{sub x}O{sub 4} first increased to 47 nm at x = 0.4 and then decreased down to 37 nm at x = 1. The main two absorption bands in IR spectra were observed around 600 cm{sup −1} and 400 cm{sup −1} corresponding to stretching vibration of tetrahedral and octahedral group Fe{sup 3+}–O{sup 2−}. Saturation magnetization and hyperfine field values decreased linearly with Al{sup 3+} due to magnetic dilution and the relative strengths of Fe–O–Me (Me = Fe, Ni, Zn, and Al) superexchanges. The coercive field showed an inverse dependence on ferrite particle size with minimum value of 82 Oe for x = 0.4. A continuous drop in Curie temperature was observed with the Al{sup 3+} substitution. From the Moessbauer spectral analysis and X-ray diffraction analysis, it is deduced that Al{sup 3+} for x < 0.4 has no obvious preference for either tetrahedral or octahedral site but has a greater preference for the B site for x > 0.4. In nutshell the study presents detailed structural and magnetic, and Moessbauer analysis of Ni{sub 0.75}Zn{sub 0.25}Fe{sub 2−x}Al{sub x}O{sub 4} ferrites.
- OSTI ID:
- 22475768
- Journal Information:
- Materials Research Bulletin, Vol. 65; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Ce{sup 3+} Ion on Structural and Hyperfine Interaction Studies of Co{sub 0.5}Ni{sub 0.5}Fe{sub 2−x}Ce{sub x}O{sub 4} Ferrites: Useful for Permanent Magnet Applications
Crystallographic and magnetic properties of the spinel-type ferrites Zn{sub x}Co{sub 1-x}Fe{sub 2}O{sub 4} (0.0 ≤ x ≤ 0.75)
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABSORPTION
ALUMINIUM ADDITIONS
CURIE POINT
DILUTION
DOPED MATERIALS
FERRITES
GRAIN SIZE
INFRARED SPECTRA
MAGNETIC PROPERTIES
MAGNETIZATION
MOESSBAUER EFFECT
NANOSTRUCTURES
NICKEL COMPOUNDS
OXIDES
PARTICLE SIZE
REDUCTION
SATURATION
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION
ZINC COMPOUNDS