Tunable photoluminescence properties of Ca{sub 8}NaLa(PO{sub 4}){sub 6}F{sub 2}:Eu{sup 2+},Mn{sup 2+} phosphor under UV excitation
Highlights: • Ca{sub 8}NaLa(PO{sub 4}){sub 6}F{sub 2}:Eu{sup 2+},Mn{sup 2+} was prepared by a combustion-assisted synthesis method. • The phosphor presents blue and yellow double color emissions. • Efficient energy transfer from Eu{sup 2+} to Mn{sup 2+} in this phosphor is observed obviously. • White emitting was realized in Ca{sub 8}NaGd(PO{sub 4}){sub 6}F{sub 2}:0.10Eu{sup 2+},0.32Mn{sup 2+},0.10B phosphor. - Abstract: A series of Eu{sup 2+} and Mn{sup 2+} coactivated Ca{sub 8}NaLa(PO{sub 4}){sub 6}F{sub 2} (CNLF) phosphors have been synthesized by a combustion-assisted synthesis method. The investigation revealed that Ca{sub 8}NaLa(PO{sub 4}){sub 6}F{sub 2} crystallized in a hexagonal crystal system with the space group P6{sub 3}/m (176). The Eu{sup 2+} activated phosphors can be efficiently excited in the range of 270–400 nm and give intense blue emission peaking at 451 nm. By codoping the Eu{sup 2+} and Mn{sup 2+} ions into the CNLF host and singly varying the doping content of the Mn{sup 2+} ion, tunable colors from blue to white and eventually to yellow are obtained in CNLF:Eu{sup 2+},Mn{sup 2+} phosphors under the irradiation of 330 nm. The energy transfer from Eu{sup 2+} to Mn{sup 2+} in CNLF:Eu{sup 2+},Mn{sup 2+} has been demonstrated to be a resonant type via a dipole–dipole mechanism and the critical distance of energy transfer from Eu{sup 2+} to Mn{sup 2+} was estimated to be about 11.9 Å. The investigation indicates that the obtained samples might have potential application in white LEDs.
- OSTI ID:
- 22475724
- Journal Information:
- Materials Research Bulletin, Vol. 64; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Phase transition and multicolor luminescence of Eu{sup 2+}/Mn{sup 2+}-activated Ca{sub 3}(PO{sub 4}){sub 2} phosphors
A novel blue luminescent material Sr{sub 6}Ca{sub 4}(PO{sub 4}){sub 6}F{sub 2}:Eu{sup 2+}
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
CALCIUM COMPOUNDS
COLOR
CRYSTALS
EUROPIUM ADDITIONS
EXCITATION
FLUORINE COMPOUNDS
HEXAGONAL LATTICES
LANTHANUM COMPOUNDS
LIGHT EMITTING DIODES
MANGANESE ADDITIONS
PHOSPHATES
PHOSPHORS
PHOTOLUMINESCENCE
SODIUM COMPOUNDS
SPACE GROUPS
SYNTHESIS
X-RAY DIFFRACTION