Synthetic and spectroscopic studies of vanadate glaserites I: Upconversion studies of doubly co-doped (Er, Tm, or Ho):Yb:K{sub 3}Y(VO{sub 4}){sub 2}
The synthesis and upconversion properties of trigonal glaserite-type K{sub 3}Y(VO{sub 4}){sub 2} co-doped with Er{sup 3+}/Yb{sup 3+}, Ho{sup 3+}/Yb{sup 3+}, or Tm{sup 3+}/Yb{sup 3+} were studied. Powder samples were synthesized by solid state reactions at 1000 °C for 48 h, while well-formed hexagonal single crystals of the same were grown hydrothermally using 10 M K{sub 2}CO{sub 3} at 560–650 °C. Infrared-to-visible upconversion by Er{sup 3+}/Yb{sup 3+}, Ho{sup 3+}/Yb{sup 3+}, or Tm{sup 3+}/Yb{sup 3+} codoped-K{sub 3}Y(VO{sub 4}){sub 2} glaserite powder and single crystals was observed, and the upconversion spectral properties were studied as a function of different Er{sup 3+}, Tm{sup 3+}, Ho{sup 3+}, and Yb{sup 3+} ion concentrations. The process is observed under 980 nm laser diode excitation and leads to strong green (552 nm) and red (659 nm) emission for Er{sup 3+}/Yb{sup 3+}, green (549 nm) and red (664 nm) emission for Ho{sup 3+}/Yb{sup 3+}, and blue (475 nm) and red (647 nm) emission for Tm{sup 3+}/Yb{sup 3+}. The main mechanism that allows for up-conversion is attributed the energy transfer among Yb{sup 3+} and the various Er{sup 3+}/Ho{sup 3+}/Tm{sup 3+} ions in excited states. These results illustrate the large potential of co-doped alkali double vanadates for photonic applications involving optoelectronics devices. - Graphical abstract: Synthesis and upconversion in vanadate glaserites. - Highlights: • K{sub 3}Y(VO{sub 4}){sub 2} codoped with Er, Tm, or Ho:Yb were synthesized via solid-state and hydrothermal routes. • Upconversion properties are investigated. • The codoped compounds revealed efficient infrared-to-visible upconversion. • The presented compounds are potential host for solid state lighting.
- OSTI ID:
- 22475669
- Journal Information:
- Journal of Solid State Chemistry, Vol. 226; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Vacuum ultraviolet and near-infrared excited luminescence properties of Ca{sub 3}(PO{sub 4}){sub 2}:RE{sup 3+}, Na{sup +} (RE=Tb, Yb, Er, Tm, and Ho)
Luminescence properties of Ca{sub 0.65}La{sub 0.35}F{sub 2.35}:Yb{sup 3+}, Er{sup 3+} with enhanced red emission via upconversion
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
CONCENTRATION RATIO
CRYSTAL GROWTH
DOPED MATERIALS
ENERGY TRANSFER
ERBIUM COMPOUNDS
ERBIUM IONS
EXCITED STATES
HOLMIUM IONS
MONOCRYSTALS
OPTOELECTRONIC DEVICES
POTASSIUM CARBONATES
POWDERS
SOLIDS
SYNTHESIS
TEMPERATURE DEPENDENCE
THULIUM IONS
VANADATES
YTTERBIUM IONS
YTTRIUM COMPOUNDS