Broadband down-conversion based near infrared quantum cutting in Eu{sup 2+}–Yb{sup 3+} co-doped SrAl{sub 2}O{sub 4} for crystalline silicon solar cells

Journal Article · Sun Mar 15 04:00:00 EDT 2015 · Journal of Solid State Chemistry

DOI:https://doi.org/10.1016/J.JSSC.2015.02.020· OSTI ID:22475662

Tai, Yuping ^[1]; Zheng, Guojun ^[1]; Wang, Hui ^[1]; Bai, Jintao ^[2]

---

1. Key Laboratory of Synthetic and Natural Functional Molecule Chemistry (Ministry of Education), College of Chemistry & Materials Science, Northwest University, Xi’an 710069 (China)
2. National Key Laboratory of Photoelectric Technology and Functional Materials Culture Base, National Photoelectric Technology and Functional Materials & Application of International Science and Technology Cooperation Base, Institute of Photonics & Photon-Technology, Northwest University, Xi'an 710069 (China)

Near infrared (NIR) quantum cutting involving the down conversion of an absorbed visible photon to emission of two NIR photons was achieved in SrAl{sub 2}O{sub 4}:0.01Eu{sup 2+}, xYb{sup 3+} (x=0, 1, 2, 5, 10, 20, 30 mol%) samples. The photoluminescence properties of samples in visible and NIR regions were measured to verify the energy transfer (ET) from Eu{sup 2+} to Yb{sup 3+}. The results demonstrated that Eu{sup 2+} was an efficient sensitizer for Yb{sup 3+} in the SrAl{sub 2}O{sub 4} host lattice. According to Gaussian fitting analysis and temperature-dependent luminescence experiments, the conclusion was drawn that the cooperative energy transfer (CET) process dominated the ET process and the influence of charge transfer state (CTS) of Yb{sup 3+} could be negligible. As a result, the high energy transfer efficiency (ETE) and quantum yield (QY) have been acquired, the maximum value approached 73.68% and 147.36%, respectively. Therefore, this down-conversion material has potential application in crystalline silicon solar cells to improve conversion efficiency. - Graphical abstract: Near infrared quantum cutting was achieved in Eu{sup 2+}–Yb{sup 3+} co-doped SrAl{sub 2}O{sub 4} samples. The cooperative energy transfer process dominated energy transfer process and high energy transfer efficiency was acquired. - Highlights: • The absorption spectrum of Eu{sup 2+} ion is strong in intensity and broad in bandwidth. • The spectra of Eu{sup 2+} in SrAl{sub 2}O{sub 4} lies in the strongest region of solar spectrum. • The cooperative energy transfer (CET) dominated the energy transfer process. • The domination of CET is confirmed by experimental analysis. • SrAl{sub 2}O{sub 4}:Eu{sup 2+},Yb{sup 3+} show high energy transfer efficiency and long lifetime.

• OSTI ID: 22475662
• Journal Information: Journal of Solid State Chemistry, Journal Name: Journal of Solid State Chemistry Vol. 226; ISSN 0022-4596; ISSN JSSCBI
• Country of Publication: United States
• Language: English

Related Subjects

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CHEMISTRY
ABSORPTION SPECTRA
ALUMINATES
COMPUTERIZED TOMOGRAPHY
CONCENTRATION RATIO
DOPED MATERIALS
ENERGY TRANSFER
EUROPIUM IONS
LIFETIME
NEAR INFRARED RADIATION
PHOTOLUMINESCENCE
PHOTOVOLTAIC CONVERSION
SENSITIZERS
SILICON SOLAR CELLS
STRONTIUM COMPOUNDS
TEMPERATURE DEPENDENCE
YTTERBIUM IONS