The Ho–Ni–Ge system: Isothermal section and new rare-earth nickel germanides

Journal Article · Fri May 15 04:00:00 EDT 2015 · Journal of Solid State Chemistry

DOI:https://doi.org/10.1016/J.JSSC.2014.12.025· OSTI ID:22475594

Knotko, A. V. ^[1]; Yapaskurt, V. O. ^[2]; Yuan, Fang; Mozharivskyj, Y. ^[3]; Pani, M.; Provino, A.; Manfrinetti, P. ^[4]

---

1. Department of Chemistry, Moscow State University, Leninskie Gory, House 1, Building 3, GSP-2, Moscow 119992 (Russian Federation)
2. Department of Petrology, Faculty of Geology, Moscow State University, Leninskie Gory, Moscow 119992 (Russian Federation)
3. Department of Chemistry and Chemical Biology, McMaster University, 1280 Main Street West, Hamilton, Ontario L8S 4M1 (Canada)
4. Institute SPIN-CNR and Dipartimento di Chimica e Chimica Industriale, Università di Genova, Via Dodecaneso 31, 16146 Genova (Italy)

The Ho–Ni–Ge system has been investigated at 1070 K and up to ~60 at% Ho by X-ray diffraction and microprobe analyses. Besides the eight known compounds, HoNi{sub 5}Ge{sub 3} (YNi{sub 5}Si{sub 3}-type), HoNi{sub 2}Ge{sub 2} (CeAl{sub 2}Ga{sub 2}-type), Ho{sub 2}NiGe{sub 6} (Ce{sub 2}CuGe{sub 6}-type), HoNiGe{sub 3} (SmNiGe{sub 3}-type), HoNi{sub 0.2÷0.6}Ge{sub 2} (CeNiSi{sub 2}-type), Ho{sub 37÷34}Ni{sub 6÷24}Ge{sub 57÷42} (AlB{sub 2}-type), HoNiGe (TiNiSi-type), Ho{sub 3}NiGe{sub 2} (La{sub 3}NiGe{sub 2}-type), the ternary system contains four new compounds: Ho{sub 3}Ni{sub 11}Ge{sub 4} (Sc{sub 3}Ni{sub 11}Ge{sub 4}-type), HoNi{sub 3}Ge{sub 2} (ErNi{sub 3}Ge{sub 2}-type), Ho{sub 3}Ni{sub 2}Ge{sub 3} (Hf{sub 3}Ni{sub 2}Si{sub 3}-type) and ~Ho{sub 5}Ni{sub 2}Ge{sub 3} (unknown structure). Quasi-binary solid solutions were observed at 1070 K for Ho{sub 2}Ni{sub 17}, HoNi{sub 5}, HoNi{sub 7}, HoNi{sub 3}, HoNi{sub 2}, HoNi and Ho{sub 2}Ge{sub 3}, but no detectable solubility was found for the other binary compounds in the Ho–Ni–Ge system. Based on the magnetization measurements, the HoNi{sub 5}Ge{sub 3}, HoNi{sub 3}Ge{sub 2} and Ho{sub 3}Ni{sub 11}Ge{sub 4} (and isostructural (Tb, Dy){sub 3}Ni{sub 11}Ge{sub 4}) compounds have been found to show paramagnetic behavior down to 5 K, whereas Ho{sub 3}Ni{sub 2}Ge{sub 3} exhibits an antiferromagnetic transition at ~7 K. Additionally, the crystal structure of the new isostructural phases (Y, Yb)Ni{sub 3}Ge{sub 2} (ErNi{sub 3}Ge{sub 2}-type), Er{sub 3}Ni{sub 11}Ge{sub 4} (Sc{sub 3}Ni{sub 11}Ge{sub 4}-type) and (Y, Tb, Dy, Er, Tm){sub 3}Ni{sub 2}Ge{sub 3} (Hf{sub 3}Ni{sub 2}Si{sub 3}-type) has been also investigated. - Graphical abstract: The Ho–Ni–Ge system has been investigated at 1070 K and up to ~60 at.% Ho by X-ray and microprobe analyses. Besides the eight known compounds, i.e. HoNi{sub 5}Ge{sub 3} (YNi{sub 5}Si{sub 3}-type), HoNi{sub 2}Ge{sub 2} (CeAl{sub 2}Ga{sub 2}-type), Ho{sub 2}NiGe{sub 6} (Ce{sub 2}CuGe{sub 6}-type), HoNiGe{sub 3} (SmNiGe{sub 3}-type), HoNi{sub 0.2÷0.6}Ge{sub 2} (CeNiSi{sub 2}-type), Ho{sub 37÷34}Ni{sub 6÷24}Ge{sub 57÷42} (AlB{sub 2}-type), HoNiGe (TiNiSi-type), Ho{sub 3}NiGe{sub 2} (La{sub 3}NiGe{sub 2}-type), the ternary system contains four new compounds: Ho{sub 3}Ni{sub 11}Ge{sub 4} (Sc{sub 3}Ni{sub 11}Ge{sub 4}-type), HoNi{sub 3}Ge{sub 2} (ErNi{sub 3}Ge{sub 2}-type), Ho{sub 3}Ni{sub 2}Ge{sub 3} (Hf{sub 3}Ni{sub 2}Si{sub 3}-type) and ~Ho{sub 5}Ni{sub 2}Ge{sub 3} (unknown structure). Quasi-binary solid solutions were found to form at 1070 K from the binary Ho{sub 2}Ni{sub 17}, HoNi{sub 5}, HoNi{sub 7}, HoNi{sub 3}, HoNi{sub 2}, HoNi and Ho{sub 2}Ge{sub 3} compounds, while no detectable solubility was observed for the other binary compounds in the Ho–Ni–Ge system. Based on the magnetization measurements, the HoNi{sub 5}Ge{sub 3}, HoNi{sub 3}Ge{sub 2} and Ho{sub 3}Ni{sub 11}Ge{sub 4} (and isostructural (Tb, Dy){sub 3}Ni{sub 11}Ge{sub 4}) compounds have been found to show paramagnetic behavior down to 5 K, whereas Ho{sub 3}Ni{sub 2}Ge{sub 3} exhibits an antiferromagnetic transition at ~7 K. Additionally, the crystal structure of the new isostructural phases (Y, Yb)Ni{sub 3}Ge{sub 2} (ErNi{sub 3}Ge{sub 2}-type), Er{sub 3}Ni{sub 11}Ge{sub 4} (Sc{sub 3}Ni{sub 11}Ge{sub 4}-type) and (Y, Tb, Dy, Er, Tm){sub 3}Ni{sub 2}Ge{sub 3} (Hf{sub 3}Ni{sub 2}Si{sub 3}-type) has been also investigated. - Highlights: • Ho–Ni–Ge system has been investigated at 1070 K and up to ~60 at% Ho. • Eight known ternary holmium nickel germanides were confirmed in Ho–Ni–Ge. • Four new holmium nickel germanides were detected in Ho–Ni–Ge. • Eight new rare earth nickel germanides were detected in (Y, Tb, Dy, Er–Yb)–Ni–Ge. • HoNi{sub 5}Ge{sub 3}, HoNi{sub 3}Ge{sub 2},(Tb, Dy, Ho){sub 3}Ni{sub 11}Ge{sub 4} and Ho{sub 3}Ni{sub 2}Ge{sub 3} are paramagnet down to 5–7 K.

• OSTI ID: 22475594
• Journal Information: Journal of Solid State Chemistry, Journal Name: Journal of Solid State Chemistry Vol. 225; ISSN 0022-4596; ISSN JSSCBI
• Country of Publication: United States
• Language: English

Related Subjects

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CHEMISTRY
ALUMINIUM BORIDES
ANTIFERROMAGNETISM
CRYSTAL STRUCTURE
GERMANIDES
HOLMIUM COMPOUNDS
MAGNETIC PROPERTIES
MAGNETIZATION
NICKEL SILICIDES
PARAMAGNETISM
PHASE DIAGRAMS
SCANDIUM COMPOUNDS
SOLID SOLUTIONS
SOLUBILITY
TEMPERATURE DEPENDENCE
X-RAY DIFFRACTION