The new silver borate Ag{sub 3}B{sub 5}O{sub 9}
Single crystals of Ag{sub 3}B{sub 5}O{sub 9} were obtained via high-pressure synthesis at 3 GPa and 600 °C, using a Walker-type multianvil high-pressure device. Ag{sub 3}B{sub 5}O{sub 9} crystalizes with a=674.7(2), b=943.5(2), c=1103.5(2) pm, V=0.7025(2) nm{sup 3}, and Z=4 in the noncentrosymmetric space group P2{sub 1}2{sub 1}2{sub 1} (no. 19). The orthorhombic structure was refined from 3740 independent reflections with R1=0.0496 and wR2=0.587 (all data). It is built up from infinite corner-sharing chains of BO{sub 4} tetrahedra along the a axis, which are interconnected by BO{sub 3} groups to form a network. In the structure, three crystallographically independent sites are occupied with Ag{sup +} cations exhibiting argentophillic interactions. The synthetic conditions as well as the results of the single crystal structure analysis are presented. - Graphical abstract: Noncentrosymmetric silver borate: During investigations in the system Ag–B–O, a new noncentrosymmetric silver borate Ag{sub 3}B{sub 5}O{sub 9} was discovered. The new structure type is built up from corner-sharing BO{sub 3} and BO{sub 4} groups, forming a network. Argentophillic interactions are clearly indicated by the Ag{sup +}⋯Ag{sup +} distances present in the structure. - Highlights: • A noncentrosymmetric borate Ag{sub 3}B{sub 5}O{sub 9} is accessible via high-pressure synthesis. • Ag{sub 3}B{sub 5}O{sub 9} is the second high-pressure silver borate. • Ag{sup +}⋯Ag{sup +} distances in Ag3B5O9 clearly indicate the presence of argentophillic interactions.
- OSTI ID:
- 22475585
- Journal Information:
- Journal of Solid State Chemistry, Vol. 225; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
High-pressure synthesis, crystal structure, and structural relationship of the first ytterbium fluoride borate Yb{sub 5}(BO{sub 3}){sub 2}F{sub 9}
High-pressure synthesis, crystal structure, and properties of the first ternary hafniumborate {beta}-HfB{sub 2}O{sub 5}