Degradation processes of reinforced concretes by combined sulfate–phosphate attack
- Inter-Departmental Research Center for the Study of Cement Materials and Hydraulic Binders (CIRCe), University of Padova, Via Gradenigo 6, 35131 Padova (Italy)
- BAM Federal Institute for Materials Research and Testing, Unter den Eichen 87, 12205 Berlin (Germany)
- Department of Geosciences, University of Padova, Via Gradenigo 6, 35131 Padova (Italy)
A novel form of alteration due to the interaction between hydrated cement phases and sulfate and phosphate-based pollutants is described, through the characterization of concrete samples from an industrial reinforced concrete building. Decalcification of the cement matrices was observed, with secondary sulfate and phosphate-based mineral formation, according to a marked mineralogical and textural zoning. Five alteration layers may be detected: the two outermost layers are characterized by the presence of gypsum–brushite solid solution phases associated with anhydrous calcium sulfates and phosphates, respectively, while a progressive increase in apatite and ammonium magnesium phosphates is observable in the three innermost layers, associated with specific apatite precursors (brushite, octacalcium phosphate and amorphous calcium phosphate, respectively). The heterogeneous microstructural development of secondary phases is related to the chemical, pH and thermal gradients in the attacked cementitious systems, caused by different sources of pollutants and the exposure to the sun's radiation.
- OSTI ID:
- 22475482
- Journal Information:
- Cement and Concrete Research, Journal Name: Cement and Concrete Research Vol. 68; ISSN 0008-8846; ISSN CCNRAI
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of Calcined Clay/Calcium Sulfate Blends for Robust Performance of LC3 Concrete
Physical-chemical-mechanical quantitative assessment of the microstructural evolution in Portland-limestone cement pastes exposed to magnesium sulfate attack at low temperature