Cathodo- and photoluminescence increase in amorphous hafnium oxide under annealing in oxygen
Journal Article
·
· Journal of Experimental and Theoretical Physics
- Ioffe Physical Technical Institute (Russian Federation)
- Ural State Technical University (Russian Federation)
- Russian Academy of Sciences, Institute of Semiconductor Physics, Siberian Branch (Russian Federation)
- Russian Academy of Sciences, Institute of Geology and Mineralogy, Siberian Branch (Russian Federation)
Cathodo- and photoluminescence of amorphous nonstoichiometric films of hafnium oxide are studied with the aim to verify the hypothesis that oxygen vacancies are responsible for the luminescence. To produce oxygen vacancies, hafnium oxide was enriched in surplus metal during synthesis. To reduce the oxygen concentration, the film was annealed in oxygen. A qualitative control of the oxygen concentration was carried out by the refractive index. In the initial, almost stoichiometric films we observed a 2.7-eV band in cathodoluminescence. Annealing in oxygen results in a considerable increase in its intensity, as well as in the appearance of new bands at 1.87, 2.14, 3.40, and 3.6 eV. The observed emission bands are supposed to be due to single oxygen vacancies and polyvacancies in hafnium oxide. The luminescence increase under annealing in an oxygen atmosphere may be a result of the emission quenching effect.
- OSTI ID:
- 22472306
- Journal Information:
- Journal of Experimental and Theoretical Physics, Journal Name: Journal of Experimental and Theoretical Physics Journal Issue: 4 Vol. 120; ISSN JTPHES; ISSN 1063-7761
- Country of Publication:
- United States
- Language:
- English
Similar Records
The origin of 2.7 eV luminescence and 5.2 eV excitation band in hafnium oxide
The Evolution of the Conductivity and Cathodoluminescence of the Films of Hafnium Oxide in the Case of a Change in the Concentration of Oxygen Vacancies
The origin of 2.7 eV blue luminescence band in zirconium oxide
Journal Article
·
Sun Feb 16 23:00:00 EST 2014
· Applied Physics Letters
·
OSTI ID:22283136
The Evolution of the Conductivity and Cathodoluminescence of the Films of Hafnium Oxide in the Case of a Change in the Concentration of Oxygen Vacancies
Journal Article
·
Mon Oct 15 00:00:00 EDT 2018
· Physics of the Solid State
·
OSTI ID:22770982
The origin of 2.7 eV blue luminescence band in zirconium oxide
Journal Article
·
Sat Dec 27 23:00:00 EST 2014
· Journal of Applied Physics
·
OSTI ID:22399167