Structural and photoluminescent properties of nanowires formed by the metal-assisted chemical etching of monocrystalline silicon with different doping level
- Lomonosov Moscow State University, Faculty of Physics (Russian Federation)
Silicon-nanowire layers grown by the metal-assisted chemical etching of (100)-oriented p-type monocrystalline silicon substrates with a resistivity of 10 and 0.001 Ω · cm are studied by electron microscopy, Raman scattering, and photoluminescence measurements. It is established that nanowires grown on lightly doped substrates are structurally nonporous and formed as crystalline cores covered by nanocrystals 3–5 nm in dimensions. Nanowires grown on heavily doped substrates are structurally porous and contain both small nanocrystals and coarser crystallites with equilibrium charge carriers that influence interband radiative recombination. It is found that the photoluminescence intensity of nanowires in the spectral range 1.3–2.0 eV depends on the presence of molecular oxygen.
- OSTI ID:
- 22469821
- Journal Information:
- Semiconductors, Journal Name: Semiconductors Journal Issue: 8 Vol. 49; ISSN SMICES; ISSN 1063-7826
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fabrication of Silicon Nanowire Forests for Thermoelectric Applications by Metal-Assisted Chemical Etching
Optical properties of nanowire structures produced by the metal-assisted chemical etching of lightly doped silicon crystal wafers
One-step synthesis of lightly doped porous silicon nanowires in HF/AgNO{sub 3}/H{sub 2}O{sub 2} solution at room temperature
Journal Article
·
Fri Dec 14 23:00:00 EST 2018
· Journal of Materials Engineering and Performance
·
OSTI ID:22971098
Optical properties of nanowire structures produced by the metal-assisted chemical etching of lightly doped silicon crystal wafers
Journal Article
·
Sun Dec 14 23:00:00 EST 2014
· Semiconductors
·
OSTI ID:22300405
One-step synthesis of lightly doped porous silicon nanowires in HF/AgNO{sub 3}/H{sub 2}O{sub 2} solution at room temperature
Journal Article
·
Fri Dec 14 23:00:00 EST 2012
· Journal of Solid State Chemistry
·
OSTI ID:22149987