Intercalation of p-methycinnamic acid anion into Zn-Al layered double hydroxide to improve UV aging resistance of asphalt
- School of Civil Engineering and Mechanics, Central South University of Forestry and Technology, Changsha 410004, Hunan (China)
- Key Laboratory of Advanced Technology for Special Functional Materials of Ministry of Education, Wuhan 430070 (China)
- State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070 (China)
A UV absorber, p-methycinnamic acid (PMCA), was intercalated into Zn-Al layered double hydroxide (LDH) by calcination recovery. Fourier transform infrared spectroscopy showed that the PMCA anions completely replaced the CO{sub 3}{sup 2−} anions in the interlayer galleries of Zn-Al-LDH containing PMCA anions (Zn-Al-PMCA-LDH). X-ray diffraction and transmission electron microscopy showed that the interlayer distance increased from 0.78 nm to 1.82 nm after the substitution of PMCA anions for CO{sub 3}{sup 2−} anions. The similar diffraction angles of the CO{sub 3}{sup 2−} anion-containing Zn-Al-LDH (Zn-Al-CO{sub 3}{sup 2−}-LDH) and the Zn-Al-CO{sub 3}{sup 2−}-LDH/styrene–butadiene–styrene (SBS) modified asphalt implied that the asphalt molecules do not enter into the LDH interlayer galleries to form separated-phase structures. The different diffraction angles of Zn-Al-PMCA-LDH and Zn-Al-PMCA-LDH/SBS modified asphalt indicated that the asphalt molecules penetrated into the LDH interlayer galleries to form an expanded-phase structure. UV-Vis absorbance analyses showed that Zn-Al-PMCA-LDH was better able to block UV light due to the synergistic effects of PMCA and Zn-Al-LDH. Conventional physical tests and atomic force microscopy images of the SBS modified asphalt, Zn-Al-CO{sub 3}{sup 2−}-LDH/SBS modified asphalt and Zn-Al-PMCA-LDH/SBS modified asphalt before and after UV aging indicated that Zn-Al-PMCA-LDH improved the UV aging resistance of SBS modified asphalts.
- OSTI ID:
- 22454460
- Journal Information:
- AIP Advances, Vol. 5, Issue 2; Other Information: (c) 2015 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of sodium dodecyl sulfate concentration on the photocatalytic activity and dielectric properties of intercalated sodium dodecyl sulfate into Zn–Cd–Al layered double hydroxide
Intercalation and controlled release properties of vitamin C intercalated layered double hydroxide