Adjustable ferromagnetic resonance frequency in CoO/CoFeB system
- CEA Le Ripault, BP16, 37260 Monts (France)
- LPS, CNRS UMR 8502, University of Paris-Sud, 91405 Orsay Cedex (France)
- LMB EA4522, University of Brest, 6 av. Le Gorgeu, 29238 Brest Cedex 3 (France)
- GREMAN, CNRS UMR 7347, University of Tours, 37200 Tours (France)
Static and dynamic properties of (CoO/CoFeB){sub n} multilayers have been investigated. An anisotropy field enhancement was evidenced when the CoO layer was deposited under the CoFeB layer. Tuning the relative CoFeB and CoO layers thicknesses, high ferromagnetic resonance frequencies up to 4 GHz were achieved. The coupling effect between the CoO and CoFeB layers was induced by a dipolar coupling due to the anisotropic roughness topology of the CoO layer. This anisotropic roughness was induced by the deposition geometry and evidenced by atomic force microscopy. The strength of the dipolar interfacial coupling was calculated thanks to Schlömann's model. Multilayer stacks were fabricated and the magnetic properties observed for the trilayers could be maintained.
- OSTI ID:
- 22412954
- Journal Information:
- Journal of Applied Physics, Vol. 117, Issue 3; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of heavy metal layer thickness on spin-orbit torque and current-induced switching in Hf|CoFeB|MgO structures
Effect of heavy metal layer thickness on spin-orbit torque and current-induced switching in Hf|CoFeB|MgO structures