Fabrication of MgAl{sub 2}O{sub 4} tunnel barrier by radio frequency-sputtering method and magnetoresistance effect through it with Fe or Fe{sub 4}N ferromagnetic electrode
Journal Article
·
· Journal of Applied Physics
- Department of Electronic Engineering, Graduate School of Engineering, Tohoku University, 6-6-05 Aobayama, Sendai 980-8579 (Japan)
Spinel MgAl{sub 2}O{sub 4} thin films were deposited on MgO single-crystal substrates and epitaxial Fe (or Fe{sub 4}N) thin films by RF-sputtering from a ceramic target. Epitaxial relationship was confirmed by X-ray diffraction analysis between the crystalline spinel MgAl{sub 2}O{sub 4} films and the respective substrate and underlayers, while no diffraction peak was observed from the films deposited on amorphous substrates. Spin-valve type magnetic tunnel junctions (MTJs) with a stacking structure of Fe [Fe{sub 4}N]/MgAl{sub 2}O{sub 4}/CoFeB/Ru/Fe/MnIr exhibited normal [inverse] tunnel magnetoresistance (TMR) effect, reflecting the sign of spin polarization of Fe [Fe{sub 4}N]. The maximum magnitude of the TMR ratio obtained for the Fe-based and Fe{sub 4}N-based MTJs was 67% and 18%, respectively. The resistance area product values of the MTJs were significantly larger than the reported values for the MTJs with a post-oxidized spinel MgAl{sub 2}O{sub 4} barrier.
- OSTI ID:
- 22410090
- Journal Information:
- Journal of Applied Physics, Journal Name: Journal of Applied Physics Journal Issue: 17 Vol. 117; ISSN JAPIAU; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
MgAl{sub 2}O{sub 4}(001) based magnetic tunnel junctions made by direct sputtering of a sintered spinel target
Perpendicular magnetic anisotropy in Ta|Co{sub 40}Fe{sub 40}B{sub 20}|MgAl{sub 2}O{sub 4} structures and perpendicular CoFeB|MgAl{sub 2}O{sub 4}|CoFeB magnetic tunnel junction
Magnetic properties of epitaxial Fe{sub 3}O{sub 4} films with various crystal orientations and tunnel magnetoresistance effect at room temperature
Journal Article
·
Mon Mar 28 00:00:00 EDT 2016
· Applied Physics Letters
·
OSTI ID:22591507
Perpendicular magnetic anisotropy in Ta|Co{sub 40}Fe{sub 40}B{sub 20}|MgAl{sub 2}O{sub 4} structures and perpendicular CoFeB|MgAl{sub 2}O{sub 4}|CoFeB magnetic tunnel junction
Journal Article
·
Mon Sep 08 00:00:00 EDT 2014
· Applied Physics Letters
·
OSTI ID:22310833
Magnetic properties of epitaxial Fe{sub 3}O{sub 4} films with various crystal orientations and tunnel magnetoresistance effect at room temperature
Journal Article
·
Mon Sep 08 00:00:00 EDT 2014
· Applied Physics Letters
·
OSTI ID:22310835