Effects of phase transformation on the microstructures and magnetostriction of Fe-Ga and Fe-Ga-Zn ferromagnetic shape memory alloys

Journal Article · Thu May 07 00:00:00 EDT 2015 · Journal of Applied Physics

DOI:https://doi.org/10.1063/1.4917185· OSTI ID:22409942

Lin, Yin-Chih; Lin, Chien-Feng ^[1]

---

1. Department of Mold and Die Engineering, National Kaohsiung University of Applied Sciences, Kaohsiung 807-78, Taiwan (China)

The phase transformation and magnetostriction of bulk Fe{sub 73}Ga{sub 27} and Fe{sub 73}Ga{sub 18}Zn{sub 9} (at. %) ferromagnetic shape memory alloys (FSMs) were investigated by transmission electron microscopy (TEM), x-ray diffraction (XRD), and a magnetostrictive-meter setup. For the Fe{sub 73}Ga{sub 27} FSM alloy solution treated at 1100 °C for 4 h and quenched in ice brine, the antiphase boundary segments of the D0{sub 3} domain were observed in the A2 (disordered) matrix, and the Fe{sub 73}Ga{sub 27} FSM alloy had an optimal magnetostriction (λ{sub ‖}{sup s }= 71 × 10{sup −6} and λ{sub ⊥}{sup s }= −31 × 10{sup −6}). In Fe{sub 73}Ga{sub 27} FSM alloy as-quenched, aged at 700 °C for 24 h, and furnace cooled, D0{sub 3} nanoclusters underwent phase transformation to an intermediate tetragonal phase (i.e., L1{sub 0}-like martensite) via Bain distortion, and finally L1{sub 2} (Fe{sub 3}Ga) structures precipitated, as observed by TEM and XRD. The L1{sub 0}-like martensite and L1{sub 2} phases in the aged Fe{sub 73}Ga{sub 27} FSM alloy drastically decreased the magnetostriction from positive to negative (λ{sub ‖}{sup s }= −20 × 10{sup −6} and λ{sub ⊥}{sup s }= −8 × 10{sup −6}). However, in Fe{sub 73}Ga{sub 18}Zn{sub 9} FSM alloy as-quenched and aged, the phase transformation of D0{sub 3} to an intermediate tetragonal martensite phase and precipitation of L1{sub 2} structures were not found. The results indicate that the aged Fe{sub 73}Ga{sub 18}Zn{sub 9} FSM alloy maintained stable magnetostriction (λ{sub ‖}{sup s }= 36 × 10{sup −6} and λ{sub ⊥}{sup s }= −31 × 10{sup −6}). Adding Zn can improve the ferromagnetic shape memory effect of aged Fe{sub 73}Ga{sub 18}Zn{sub 9} alloy, which may be useful in application of the alloy in high temperature environments.

• OSTI ID: 22409942
• Journal Information: Journal of Applied Physics, Journal Name: Journal of Applied Physics Journal Issue: 17 Vol. 117; ISSN JAPIAU; ISSN 0021-8979
• Country of Publication: United States
• Language: English

Related Subjects

75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
DOMAIN STRUCTURE
FERROMAGNETIC MATERIALS
FERROMAGNETISM
GALLIUM ALLOYS
IRON BASE ALLOYS
MAGNETOSTRICTION
MARTENSITE
MICROSTRUCTURE
NANOSTRUCTURES
PHASE TRANSFORMATIONS
SHAPE MEMORY EFFECT
TEMPERATURE DEPENDENCE
TETRAGONAL LATTICES
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION
ZINC ALLOYS