The origin of deep-level impurity transitions in hexagonal boron nitride
Deep ultraviolet photoluminescence (PL) emission spectroscopy has been employed to investigate the origin of the widely observed deep level impurity related donor-acceptor pair (DAP) transition with an emission peak near 4.1 eV in hexagonal boron nitride (h-BN). A set of h-BN epilayers were grown by metal-organic chemical vapor deposition (MOCVD) under different ammonia (NH{sub 3}) flow rates to explore the role of nitrogen vacancies (V{sub N}) in the deep-level transitions. The emission intensity of the DAP transition near 4.1 eV was found to decrease exponentially with an increase of the NH{sub 3} flow rate employed during the MOCVD growth, implying that impurities involved are V{sub N}. The temperature-dependent PL spectra were measured from 10 K up to 800 K, which provided activation energies of ∼0.1 eV for the shallow impurity. Based on the measured energy level of the shallow impurity (∼0.1 eV) and previously estimated bandgap value of about 6.5 eV for h-BN, we deduce a value of ∼2.3 eV for the deep impurity involved in this DAP transition. The measured energy levels together with calculation results and formation energies of the impurities and defects in h-BN suggest that V{sub N} and carbon impurities occupying the nitrogen sites, respectively, are the most probable shallow donor and deep acceptor impurities involved in this DAP transition.
- OSTI ID:
- 22399080
- Journal Information:
- Applied Physics Letters, Vol. 106, Issue 2; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Origin and roles of oxygen impurities in hexagonal boron nitride epilayers
Probing carbon impurities in hexagonal boron nitride epilayers
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ACTIVATION ENERGY
AMMONIA
BORON NITRIDES
CARBON
CHEMICAL VAPOR DEPOSITION
EMISSION SPECTROSCOPY
ENERGY LEVELS
EV RANGE
FLOW RATE
FORMATION HEAT
IMPURITIES
NITROGEN
ORGANOMETALLIC COMPOUNDS
PHOTOLUMINESCENCE
TEMPERATURE DEPENDENCE
ULTRAVIOLET RADIATION
VACANCIES