Effect of transition metal salts on the initiated chemical vapor deposition of polymer thin films
Journal Article
·
· Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films
- Mork Family Department of Chemical Engineering and Materials Science, University of Southern California, 925 Bloom Walk, Los Angeles, California 90089 (United States)
In this work, the effect of transition metal salts on the initiated chemical vapor deposition of polymer thin films was studied using x-ray photoelectron spectroscopy. The polymerizations of 4-vinyl pyridine and 1H,1H,2H,2H-perfluorodecyl acrylate were studied using copper(II) chloride (CuCl{sub 2}) and iron(III) chloride (FeCl{sub 3}) as the transition metal salts. It was found that the surface coverages of both poly(4-vinyl pyridine) (P4VP) and poly(1H,1H,2H,2H-perfluorodecyl acrylate) were decreased on CuCl{sub 2}, while the surface coverage of only P4VP was decreased on FeCl{sub 3}. The decreased polymer surface coverage was found to be due to quenching of the propagating radicals by the salt, which led to a reduction of the oxidation state of the metal. The identification of this reaction mechanism allowed for tuning of the effectiveness of the salts to decrease the polymer surface coverage through the adjustment of processing parameters such as the filament temperature. Additionally, it was demonstrated that the ability of transition metal salts to decrease the polymer surface coverage could be extended to the fabrication of patterned cross-linked coatings, which is important for many practical applications such as sensors and microelectronics.
- OSTI ID:
- 22392178
- Journal Information:
- Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films, Journal Name: Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films Journal Issue: 3 Vol. 33; ISSN 0734-2101; ISSN JVTAD6
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydrogen bonding directed co-assembly of polyoxometalates and polymers to core–shell nanoparticles
Polymeric coordination complexes based on cobalt, nickel, and ruthenium that exhibit synergistic thermal properties
Journal Article
·
Wed Sep 12 20:00:00 EDT 2018
· Materials Chemistry Frontiers
·
OSTI ID:1493752
Polymeric coordination complexes based on cobalt, nickel, and ruthenium that exhibit synergistic thermal properties
Conference
·
Thu Dec 30 23:00:00 EST 1993
·
OSTI ID:141944