Spectroscopic properties of erbium-doped yttria-stabilised zirconia crystals
Journal Article
·
· Quantum Electronics (Woodbury, N.Y.)
- N.P. Ogarev Mordovian State University, Saransk (Russian Federation)
- A M Prokhorov General Physics Institute, Russian Academy of Sciences, Moscow (Russian Federation)
Yttria-stabilised zirconia crystals ZrO{sub 2} – Y{sub 2}O{sub 3} (6 mol %) – Er{sub 2}O{sub 3} (5.85 mol %) are grown by directional crystallisation in a cold container using direct RF melting. The spectral and luminescent properties of these crystals are studied in order to use them as active media of solid state lasers emitting in the wavelength range 1.5 – 1.7 μm. (active media)
- OSTI ID:
- 22373582
- Journal Information:
- Quantum Electronics (Woodbury, N.Y.), Journal Name: Quantum Electronics (Woodbury, N.Y.) Journal Issue: 2 Vol. 44; ISSN 1063-7818
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of yttria content on the preparation of nanocrystalline yttria-doped zirconia
A sol-powder coating technique for fabrication of yttria stabilised zirconia
Formation of alumina/zirconia (3 mol% yttria) composite powders prepared by the hydrazine method
Journal Article
·
Tue Feb 28 23:00:00 EST 1995
· Journal of Materials Research
·
OSTI ID:46339
A sol-powder coating technique for fabrication of yttria stabilised zirconia
Journal Article
·
Thu Aug 10 00:00:00 EDT 2006
· Materials Research Bulletin
·
OSTI ID:20895246
Formation of alumina/zirconia (3 mol% yttria) composite powders prepared by the hydrazine method
Journal Article
·
Mon Aug 01 00:00:00 EDT 1994
· Journal of the American Ceramic Society; (United States)
·
OSTI ID:7153520