Preparation and lithium intercalation behavior of TiO{sub 2} in aqueous solutions
Highlights: • The poor crystalline anatase phase or amorphous TiO{sub 2} was prepared by TiCl{sub 4} hydrolysis under different pH conditions. • Phase transition behavior and lithium intercalation ability of the obtained TiO{sub 2} were found to be related to TiO{sub 2} property. • The results indicate that TiO{sub 2} products obtained from TiCl{sub 4} hydrolysis at lower pH are favorable for lithium intercalation. - Abstract: The low crystalline or amorphous TiO{sub 2} was prepared by TiCl{sub 4} hydrolysis in aqueous solutions under different pH conditions at 45 °C. The products obtained at lower pH (1.23–3.10) appear to be nano-sized particles with poor crystalline anatase structure and an uniform particle size distribution, while the product prepared at pH 4.10 presents in a poor crystalline anatase structure and the regular morphology starts to disappear, and the products obtained at higher pH (>6.00) are amorphous and irregular morphology. The hydrolysis products obtained at pH 2.60 and 8.80 were heat-treated at 300, 400, 600, 700 and 800 °C for 3 h, respectively, to figure out the phase transition. The differences in phase transition process were observed, which verified the properties difference. The lithium intercalation abilities of the obtained TiO{sub 2} were studied. The results indicated that the TiO{sub 2} obtained at lower pH are more favorable for lithium intercalation and are better precursors.
- OSTI ID:
- 22345262
- Journal Information:
- Materials Research Bulletin, Journal Name: Materials Research Bulletin Vol. 52; ISSN MRBUAC; ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
In situ X-ray diffraction of lithium intercalation in nanostructured and thin film anatase TiO{sub 2}
Solid-state diffusive amorphization in TiO{sub 2}/ZrO{sub 2} bilayers