NaYF{sub 4}:Er,Yb/Bi{sub 2}MoO{sub 6} core/shell nanocomposite: A highly efficient visible-light-driven photocatalyst utilizing upconversion
Highlights: • Design and synthesis of NaYF{sub 4}:Er,Yb/Bi{sub 2}MoO{sub 6} based on upconversion. • NaYF{sub 4}:Er,Yb/Bi{sub 2}MoO{sub 6} nanocomposite was prepared for the first time. • Core–shell structure benefits the properties. • Upconversion contributed to the enhanced photocatalytic activity. • Helps to understand the functionality of new type photocatalysts. - Abstract: NaYF{sub 4}:Er,Yb/Bi{sub 2}MoO{sub 6} core/shell nanocomposite was designed and prepared for the first time based on upconversion. The products were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), high resolution TEM (HRTEM), energy dispersive X-ray spectroscopy (EDS) and diffuse reflectance spectra (DRS). The results revealed that the as-synthesized NaYF{sub 4}:Er,Yb/Bi{sub 2}MoO{sub 6} consisted of spheres with a core diameter of about 26 nm and a shell diameter of around 6 nm. The core was upconversion illuminant NaYF{sub 4}:Er,Yb and the shell was Bi{sub 2}MoO{sub 6} around the core, which was confirmed by EDS. The NaYF{sub 4}:Er,Yb/Bi{sub 2}MoO{sub 6} exhibited higher photocatalytic activity for the photodecomposition of Rhodamine B (RhB) under the irradiation of Xe lamp and green light emitting diode (g-LED). The mechanism of the high photocatalytic activity was discussed by photoluminescence spectra (PL), which is mainly attributed to upconversion of NaYF{sub 4}:Er,Yb in the NaYF{sub 4}:Er,Yb/Bi{sub 2}MoO{sub 6} nanocomposite and the core–shell structure.
- OSTI ID:
- 22345256
- Journal Information:
- Materials Research Bulletin, Journal Name: Materials Research Bulletin Vol. 52; ISSN MRBUAC; ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Er{sup 3+}/Yb{sup 3+}co-doped bismuth molybdate nanosheets upconversion photocatalyst with enhanced photocatalytic activity
Fast synthesis of sub-10 nm β-NaYF4:Yb3+, Er3+@NaYF4 core-shell upconversion nanocrystals mediated by oleate ligands