Photocatalytic performances of BiFeO{sub 3} particles with the average size in nanometer, submicrometer, and micrometer

Journal Article · Sat Feb 01 04:00:00 EST 2014 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2013.11.039· OSTI ID:22345226

Hao, Chunxue; FushengWen,; Xiang, Jianyong; Hou, Hang; Lv, Weiming; Lv, Yifei; Hu, Wentao; Liu, Zhongyuan

Highlights: • Three different synthesis routes have been taken to successfully prepare the BiFeO{sub 3} particles with the different morphologies and average size in 50, 500 nm, and 15 μm. • For photodegradation of dyes under visible irradiation in the presence of BiFeO{sub 3}, the photocatalytic efficiency increases quickly with the decrease in size. • The enhanced photocatalytic efficiency of BiFeO{sub 3} nanoparticles may attribute to more surface active catalytic-sites and shorter distances carriers have to migrate to the surface reaction sites. - Abstract: Three different synthesis routes were taken to successfully prepare the BiFeO{sub 3} particles with the different morphologies and average size in 50, 500 nm, and 15 μm, respectively. The crystal structure was recognized to be a distorted rhombohedral one with the space group R3c. With the decrease in particle size, obvious decrease in peak intensity and redshift in peak position were observed for the Raman active bands. The narrow band gap was determined from the UV–vis absorption spectra, indicating the semiconducting nature of the BiFeO{sub 3}. For photodegradation of dyes under visible irradiation in the presence of BiFeO{sub 3}, the photocatalytic efficiency increased quickly with the decrease in size which may attribute to more surface active catalytic-sites and shorter distances carriers had to migrate to the surface reaction sites.

• OSTI ID: 22345226
• Journal Information: Materials Research Bulletin, Journal Name: Materials Research Bulletin Vol. 50; ISSN MRBUAC; ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ABSORPTION SPECTRA
CERAMICS
EFFICIENCY
IRRADIATION
NANOPARTICLES
PARTICLE SIZE
PEAKS
PHOTOCATALYSIS
SOL-GEL PROCESS
SPACE GROUPS
SURFACES
SYNTHESIS
TRIGONAL LATTICES
X-RAY DIFFRACTION