Photoluminescence emission at room temperature in zinc oxide nano-columns

Journal Article · Sat Feb 01 00:00:00 EST 2014 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2013.09.049· OSTI ID:22345196

Rocha, L. S.R.; Deus, R. C. ^[1]; Foschini, C. R. ^[2]; Moura, F.; Garcia, F. Gonzalez ^[3]

---

1. Universidade Estadual Paulista – Unesp, Faculdade de Engenharia de Guaratinguetá, Av. Dr. Ariberto Pereira da Cunha, 333, Bairro Portal das Colinas, CEP 12516-410 Guaratinguetá, SP (Brazil)
2. Universidade Estadual Paulista – Unesp, Instituto de Química, Laboratório Interdisciplinar em Cerâmica (LIEC), Rua Professor Francisco Degni s/n, CEP 14800-90 Araraquara, SP (Brazil)
3. Universidade Federal de Itajubá – Unifei, Campus Itabira, Rua São Paulo, 377, Bairro Amazonas, CEP 35900-37 Itabira, MG (Brazil)

Highlights: • ZnO nanoparticles were obtained by microwave-hydrothermal method. • X-ray diffraction reveals a hexagonal structure. • Photoluminescence emission evidenced two absorption peaks, at around 480 nm and 590 nm wavelengths. - Abstract: Hydrothermal microwave method (HTMW) was used to synthesize crystalline zinc oxide (ZnO) nano-columns at the temperature of 120 °C with a soaking time of 8 min. ZnO nano-columns were characterized by using X-ray analyses (XRD), infrared spectroscopy (FT-IR), thermogravimetric analyses (TG-DTA), field emission gun and transmission electron microscopy (FEG-SEM and TEM) and photoluminescence properties (PL). XRD results indicated that the ZnO nano-columns are free of any impurity phase and crystallize in the hexagonal structure. Typical FT-IR spectra for ZnO nano-columns presented well defined bands, indicating a substantial short-range order in the system. PL spectra consist of a broad band at 590 nm and narrow band at 480 nm corresponding to a near-band edge emission related to the recombination of excitons and level emission related to structural defects. These results show that the HTMW synthesis route is rapid, cost effective, and could be used as an alternative to obtain ZnO nano-columns in the temperature of 120 °C for 8 min.

• OSTI ID: 22345196
• Journal Information: Materials Research Bulletin, Vol. 50; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
77 NANOSCIENCE AND NANOTECHNOLOGY
ABSORPTION
ABSORPTION SPECTROSCOPY
CRYSTAL STRUCTURE
DIFFERENTIAL THERMAL ANALYSIS
FIELD EMISSION
FOURIER TRANSFORMATION
HYDROTHERMAL SYNTHESIS
INFRARED SPECTRA
MICROWAVE RADIATION
NANOPARTICLES
NANOSTRUCTURES
PHOTOLUMINESCENCE
SCANNING ELECTRON MICROSCOPY
THERMAL GRAVIMETRIC ANALYSIS
TRANSMISSION ELECTRON MICROSCOPY
X RADIATION
X-RAY DIFFRACTION
ZINC OXIDES