Morphology-controlled synthesis of Ag{sub 3}PO{sub 4} nano/microcrystals and their antibacterial properties
- Key Laboratory of Functional Inorganic Material Chemistry, Ministry of Education of the People's Republic of China, School of Chemistry and Materials, Heilongjiang University, Harbin 150080 (China)
- Heilongjiang Key Laboratory of Microbiology, School of Life Science, Heilongjiang University, Harbin 150080 (China)
Graphical abstract: The Ag{sub 3}PO{sub 4} with rhombic dodecahedral, spherical and small size particles were controllable fabricated just by changing the types of the solvent. The materials possess good antibacterial properties toward different kinds of bacteria. - Highlights: • The Ag{sub 3}PO{sub 4} with three morphologies were controllable fabricated. • The Ag{sub 3}PO{sub 4} as-prepared possess obvious antibacterial properties in the dark. • The antibacterial ability of Ag{sub 3}PO{sub 4} could be greatly improved under the visible light irradiation. - Abstract: We reported the controllable fabrication of Ag{sub 3}PO{sub 4} nano/microcrystals through a simple solution-based precipitation reaction. The samples were characterized by X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy and infrared spectroscopy. The results indicated that the Ag{sub 3}PO{sub 4} crystals with three different morphology, including the rhombic dodecahedron of 500 nm, the sphere of 100 nm and the particles with small-size of 20 nm, could be obtained in the solvents of water, ethylene glycol (EG) and dimethyl sulfoxide (DMSO). The antibacterial assay showed that all samples possess obvious antibacterial properties. In addition, the Ag{sub 3}PO{sub 4} with small size of 20 nm showed better activity due to their high specific surface areas. Notably, we have found that the antibacterial ability of Ag{sub 3}PO{sub 4} could be greatly improved under the visible light irradiation, which are superior to that in the dark and commercial streptomycin.
- OSTI ID:
- 22341747
- Journal Information:
- Materials Research Bulletin, Vol. 48, Issue 9; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
A chemical bath deposition route to facet-controlled Ag{sub 3}PO{sub 4} thin films with improved visible light photocatalytic activity
Optical properties of silver, silver sulfide and silver selenide nanoparticles and antibacterial applications