Crystallization of belite–melilite clinker minerals in the presence of liquid phase
- Central Research Laboratory, Taiheiyo Cement Corporation, Chiba 285-8655 (Japan)
- Department of Earth and Planetary Science, Graduate School of Science, The University of Tokyo, Tokyo 113-0033 (Japan)
- Department of Materials Science and Engineering, Nagoya Institute of Technology, Nagoya 466-8555 (Japan)
Crystallization of belite–melilite clinker minerals was studied from the view point of a high temperature equilibrium. Ca{sub 2}SiO{sub 4}–Ca{sub 2}Al{sub 2}SiO{sub 7} and Ca{sub 2}SiO{sub 4}–Ca{sub 2}AlFeSiO{sub 7} clinkers were synthesized at 1330 °C–1650 °C. The constituent phases were determined by X-ray powder diffractometry and optical microscopy. Chemical compositions of the individual clinker minerals were determined using an electron probe microanalyzer. We established the two types of P{sub 2}O{sub 5}-bearing pseudobinary phase diagrams in the systems Ca{sub 2}SiO{sub 4}–Ca{sub 2}Al{sub 2}SiO{sub 7} at 1505 °C–1650 °C and Ca{sub 2}SiO{sub 4}–Ca{sub 2}(Al,Fe){sub 2}SiO{sub 7} at 1330 °C–1550 °C. In the latter system, the liquid phase appeared at 1390 °C, which is approximately 150 °C lower than the temperature of liquid formation in the former system. The melilite phenocrysts larger than 50 μm were observed not only in the slowly cooled Ca{sub 2}SiO{sub 4}–Ca{sub 2}(Al,Fe){sub 2}SiO{sub 7} clinker but also in commercial belite–melilite clinkers. These crystals would be nucleated and grown from a liquid phase which was formed at relatively low temperatures.
- OSTI ID:
- 22323144
- Journal Information:
- Cement and Concrete Research, Vol. 60; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0008-8846
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mineralogical phase analysis of alkali and sulfate bearing belite rich laboratory clinkers
Aluminum-rich belite sulfoaluminate cements: Clinkering and early age hydration