High frequency electromagnetic properties of interstitial-atom-modified Ce{sub 2}Fe{sub 17}N{sub X} and its composites

Journal Article · Mon Jul 14 00:00:00 EDT 2014 · Applied Physics Letters

DOI:https://doi.org/10.1063/1.4889806· OSTI ID:22311092

Li, L. Z.; Wei, J. Z.; Xia, Y. H.; Wu, R.; Yun, C.; Yang, Y. B.; Yang, W. Y.; Du, H. L.; Han, J. Z.; Liu, S. Q.; Yang, Y. C.

The magnetic and microwave absorption properties of the interstitial atom modified intermetallic compound Ce{sub 2}Fe{sub 17}N{sub X} have been investigated. The Ce{sub 2}Fe{sub 17}N{sub X} compound shows a planar anisotropy with saturation magnetization of 1088 kA/m at room temperature. The Ce{sub 2}Fe{sub 17}N{sub X} paraffin composite with a mass ratio of 1:1 exhibits a permeability of μ′ = 2.7 at low frequency, together with a reflection loss of −26 dB at 6.9 GHz with a thickness of 1.5 mm and −60 dB at 2.2 GHz with a thickness of 4.0 mm. It was found that this composite increases the Snoek limit and exhibits both high working frequency and permeability due to its high saturation magnetization and high ratio of the c-axis anisotropy field to the basal plane anisotropy field. Hence, it is possible that this composite can be used as a high-performance thin layer microwave absorber.

• OSTI ID: 22311092
• Journal Information: Applied Physics Letters, Vol. 105, Issue 2; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
• Country of Publication: United States
• Language: English

Related Subjects

75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABSORPTION
ANISOTROPY
ATOMS
CERIUM COMPOUNDS
GHZ RANGE
INTERMETALLIC COMPOUNDS
IRON COMPOUNDS
MAGNETIZATION
MASS
MICROWAVE RADIATION
NITROGEN COMPOUNDS
PERMEABILITY
REFLECTION
TEMPERATURE RANGE 0273-0400 K
THICKNESS
THIN FILMS