Effect of current compliance and voltage sweep rate on the resistive switching of HfO{sub 2}/ITO/Invar structure as measured by conductive atomic force microscopy
- Department of Electrical Engineering, National Chi Nan University, Puli, Nantou, Taiwan (China)
- Department of Applied Materials and Optoelectronic Engineering, National Chi Nan University, Puli, Nantou, Taiwan (China)
The electrical characterization of HfO{sub 2}/ITO/Invar resistive switching memory structure was studied using conductive atomic force microscopy (AFM) with a semiconductor parameter analyzer, Agilent 4156C. The metal alloy Invar was used as the metal substrate to ensure good ohmic contact with the substrate holder of the AFM. A conductive Pt/Ir AFM tip was placed in direct contact with the HfO{sub 2} surface, such that it acted as the top electrode. Nanoscale current-voltage (I-V) characteristics of the HfO{sub 2}/ITO/Invar structure were measured by applying a ramp voltage through the conductive AFM tip at various current compliances and ramp voltage sweep rates. It was found that the resistance of the low resistance state (RLRS) decreased with increasing current compliance value, but resistance of high resistance state (RHRS) barely changed. However, both the RHRS and RLRS decreased as the voltage sweep rate increased. The reasons for this dependency on current compliance and voltage sweep rate are discussed.
- OSTI ID:
- 22299909
- Journal Information:
- Applied Physics Letters, Journal Name: Applied Physics Letters Journal Issue: 24 Vol. 104; ISSN APPLAB; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
In-operando hard X-ray photoelectron spectroscopy study on the impact of current compliance and switching cycles on oxygen and carbon defects in resistive switching Ti/HfO{sub 2}/TiN cells
Scanning tunneling microscopy study of nitrogen incorporated HfO{sub 2}
Improvement of Ohmic contacts on Ga2O3 through use of ITO-interlayers
Journal Article
·
Wed May 28 00:00:00 EDT 2014
· Journal of Applied Physics
·
OSTI ID:22304325
Scanning tunneling microscopy study of nitrogen incorporated HfO{sub 2}
Journal Article
·
Mon Sep 15 00:00:00 EDT 2008
· Journal of Applied Physics
·
OSTI ID:21182644
Improvement of Ohmic contacts on Ga2O3 through use of ITO-interlayers
Journal Article
·
Mon Oct 02 20:00:00 EDT 2017
· Journal of Vacuum Science and Technology B
·
OSTI ID:1399521