Real time synchrotron X-ray observations of solidification in hypoeutectic Al–Si alloys
Journal Article
·
· Materials Characterization
- Nihon Superior Centre for the Manufacture of Electronic Materials, The University of Queensland, Brisbane, QLD 4072 (Australia)
- Department of Adaptive Machine Systems, Osaka University, Suita, Osaka, 565-0871 (Japan)
- School of Mechanical and Mining Engineering, The University of Queensland, Brisbane, QLD 4072 (Australia)
- Japan Synchrotron Radiation Research Institute, SPring-8, Sayo, Hyogo, 679-5198 (Japan)
This paper demonstrates how recent advances in synchrotron technology have allowed for the real-time X-ray imaging of solidification in Al–Si alloys, despite the small difference in atomic number of these elements. The experiments performed at the SPring-8 synchrotron, involved imaging the solidification of Al–1wt.%Si and Al–4wt.%Si alloys under a low-temperature gradient and a cooling rate of around 0.3 °C/s. The nucleation and growth of the primary aluminum grains as well as the onset of eutectic solidification were clearly observed. In the alloys containing Al–4wt.%Si, contrast was sufficient to characterize the nucleation rate and growth velocity of the aluminum grains. The importance of improving observation of solidification in the Al–Si system by increasing the time resolution during critical events is discussed. - Highlights: • A synchrotron technique was used to observe solidification of Al-Si alloys. • Nucleation, coarsening, and the onset of eutectic solidification were observed. • Images captured are suitable for quantitative analysis. • The resolution that was obtained should be possible for most aluminum alloys.
- OSTI ID:
- 22288684
- Journal Information:
- Materials Characterization, Journal Name: Materials Characterization Vol. 85; ISSN 1044-5803; ISSN MACHEX
- Country of Publication:
- United States
- Language:
- English
Similar Records
Eutectic nucleation in hypoeutectic Al-Si alloys
Heterogeneous nucleation of solidification of Si in Al-Si and Al-Si-P alloys
In-Situ Synchrotron X-Ray Diffraction of Ultrasonic Microstructural Refinement During Solidification in a Commercial Al–Si–Mg Alloy
Journal Article
·
Wed Oct 15 00:00:00 EDT 2008
· Materials Characterization
·
OSTI ID:21137467
Heterogeneous nucleation of solidification of Si in Al-Si and Al-Si-P alloys
Journal Article
·
Tue Aug 01 00:00:00 EDT 1995
· Acta Metallurgica et Materialia
·
OSTI ID:100618
In-Situ Synchrotron X-Ray Diffraction of Ultrasonic Microstructural Refinement During Solidification in a Commercial Al–Si–Mg Alloy
Journal Article
·
Wed Sep 03 20:00:00 EDT 2025
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:3001358