Microstructure heterogeneity after the ECAP process and its influence on recrystallization in aluminium
Journal Article
·
· Materials Characterization
The main purpose of the present work is to describe the qualitative and quantitative behaviours of aluminium during high strain plastic deformation and the effect of deformation on the subsequent recrystallization process. An Electron Backscatter Diffraction analysis of aluminium after the Equal channel angular pressing (ECAP) and recrystallization process is presented. In order to do this, several topological maps are measured for samples processed by 4 and 8 passes and recrystallized. The processing was conducted with route C. For all samples, distributions of grain size, misorientation, image quality factor (IQ) and texture were preceded and then analysed in some detail. - Highlights: ► Describe the microstructure fragmentation in aluminum. ► High strain plastic deformation and effect of deformation on recrystallization. ► The microstructure fragmentation and its influence on recrystallization. ► Image quality factor and misorientation characteristics are examined using EBSD.
- OSTI ID:
- 22285032
- Journal Information:
- Materials Characterization, Journal Name: Materials Characterization Vol. 78; ISSN 1044-5803; ISSN MACHEX
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigation of plastic deformation heterogeneities in duplex steel by EBSD
Microstructure quantification and correlation with flow stress of ultrafine grained commercially pure Al fabricated by equal channel angular pressing (ECAP)
The transition from discontinuous to continuous recrystallization in some aluminium alloys I - the deformed state
Journal Article
·
Wed Nov 14 23:00:00 EST 2012
· Materials Characterization
·
OSTI ID:22163142
Microstructure quantification and correlation with flow stress of ultrafine grained commercially pure Al fabricated by equal channel angular pressing (ECAP)
Journal Article
·
Mon Sep 15 00:00:00 EDT 2008
· Materials Characterization
·
OSTI ID:21140773
The transition from discontinuous to continuous recrystallization in some aluminium alloys I - the deformed state
Journal Article
·
Mon Jun 21 00:00:00 EDT 2004
· Acta Materialia
·
OSTI ID:20634710