Optical and magneto-optical properties of Co-doped CeO{sub 2−δ} films in the 0.5 to 4 eV range
- Faculty of Mathematics and Physics, Charles University in Prague, Ke Karlovu 5, 12116 Prague (Czech Republic)
- Faculty of Chemical Technology, University of Pardubice, 53210 Pardubice (Czech Republic)
- Department of Materials Science and Engineering, Massachusetts Institute of Technology, Cambridge, Massachusetts 02139 (United States)
Magnetically doped Ce{sub 1−x}Co{sub x}O{sub 2−δ} (nominal x = 0.05 and 0.10) films were systematically studied by spectroscopic ellipsometry and magneto-optical spectroscopy. The samples were prepared by pulsed laser deposition on MgO(100) substrates and grew as textured polycrystalline films with thickness between 200 and 750 nm. They exhibited room temperature ferromagnetism and an out-of-plane easy axis attributed to magnetoelastic effects from the in-plane compressive strain. The dispersion of dielectric function of Ce{sub 1−x}Co{sub x}O{sub 2−δ} films was parametrized by the sum of Tauc-Lorentz and damped Lorentz oscillators and adjusted numerically. Deduced optical band gaps were similar to those of pure CeO{sub 2}, but the Co doping increased the optical absorption. The magneto-optical spectroscopy was carried out in both Faraday and Kerr configurations in the photon energy range from 0.5 to 4 eV, showing a strong dependence of the magneto-optical effect on the Co content near the optical band edge.
- OSTI ID:
- 22273729
- Journal Information:
- Journal of Applied Physics, Vol. 115, Issue 17; Conference: 55. annual conference on magnetism and magnetic materials, Atlanta, GA (United States), 14-18 Nov 2010; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magneto-optical spectroscopy of Co{sub 2}FeSi Heusler compound
Fabrication and characterization of Bismuth-Cerium composite iron garnet epitaxial films for magneto optical applications
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABSORPTION SPECTROSCOPY
CERIUM OXIDES
DIELECTRIC MATERIALS
DOPED MATERIALS
ELLIPSOMETRY
ENERGY BEAM DEPOSITION
FERROMAGNETISM
LASER RADIATION
MAGNESIUM OXIDES
MAGNETO-OPTICAL EFFECTS
OPTICAL PROPERTIES
OSCILLATORS
PHOTONS
POLYCRYSTALS
PULSED IRRADIATION
SUBSTRATES
TEMPERATURE RANGE 0273-0400 K
THIN FILMS