Temperature dependence of the magnetostriction in polycrystalline PrFe{sub 1.9} and TbFe{sub 2} alloys: Experiment and theory
- National Laboratory of Microstructures and Department of Physics, Institute of Materials Engineering, Nanjing University, Nanjing 210093 (China)
- High Magnetic Field Laboratory, Chinese Academy of Sciences (CAS), Hefei, Anhui 230031 (China)
A remarkable magnetostriction λ{sub 111} as large as 6700 ppm was found at 70 K in PrFe{sub 1.9} alloy. This value is even larger than the theoretical maximum of 5600 ppm estimated by the Steven's equivalent operator method. The temperature dependence of λ{sub 111} for PrFe{sub 1.9} and TbFe{sub 2} alloys follows well with the single-ion theory rule, which yields giant estimated λ{sub 111} values of about 8000 and 4200 ppm for PrFe{sub 1.9} and TbFe{sub 2} alloys, respectively, at 0 K. The easy magnetization direction of PrFe{sub 1.9} changes from [111] to [100] as temperature decreases, which leads to the abnormal decrease of the magnetostriction λ. The rare earth sublattice moment increases sharply in PrFe{sub 1.9} alloy with decreasing temperature, resulting in the remarkably largest estimated value of λ{sub 111} at 0 K according to the single-ion theory.
- OSTI ID:
- 22273471
- Journal Information:
- Journal of Applied Physics, Vol. 115, Issue 17; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetostriction of single crystal and polycrystal rare earth--Fe$sub 2$ compounds
Enhanced magnetostrictive effect in epoxy-bonded Tb{sub x}Dy{sub 0.9−x}Nd{sub 0.1}(Fe{sub 0.8}Co{sub 0.2}){sub 1.93} pseudo 1–3 particulate composites