Surfactant free hydrothermal synthesis of SnO{sub 2} nanorods with their microstructure and Raman studies

Journal Article · Thu Apr 24 04:00:00 EDT 2014 · AIP Conference Proceedings

DOI:https://doi.org/10.1063/1.4872680· OSTI ID:22269514

Amutha, A. ^[1]; Panigrahi, B. K.; Amirthapanian, S. ^[2]

---

1. Centre for Nanoscience and Technology, Pondicherry University, RV Nagar, Kalapet, Pondicherry- 605014, India and Materials Physics Division, Materials Science Group, Indira Gandhi Center for Atomic Research, Kalpakkam-603 102 (India)
2. Materials Physics Division, Materials Science Group, Indira Gandhi Center for Atomic Research, Kalpakkam-603 102 (India)

SnO{sub 2} nanorods were prepared by hydrothermal method without any surfactant. Their microstructure was studied with X-ray diffraction, Raman scattering and transmission electron microscopy. The range of nanorods diameter size is ∼3 to 19 nm. The crystal structure was confirmed to be SnO{sub 2} rutile tetragonal structure. The nanorods were single crystalline in nature as confirmed by HRTEM. Electron energy loss studies were carried out. EELS analysis showed presence SnO{sub 2} phase and SnO phase was not observed. New Raman modes (352 and 579 cm{sup −1}) corresponding to small size effects were observed for the SnO{sub 2} nanorods.

• OSTI ID: 22269514
• Journal Information: AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1591; ISSN APCPCS; ISSN 0094-243X
• Country of Publication: United States
• Language: English

Related Subjects

77 NANOSCIENCE AND NANOTECHNOLOGY
ENERGY-LOSS SPECTROSCOPY
HYDROTHERMAL SYNTHESIS
MICROSTRUCTURE
MONOCRYSTALS
NANOSTRUCTURES
PARTICLE SIZE
RAMAN EFFECT
TETRAGONAL LATTICES
TIN OXIDES
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION