Assignments of the Raman modes of monoclinic erbium oxide
- Department of Physics, University of Science and Technology Beijing, Beijing 100083 (China)
As a heavy rare earth oxide, erbium oxide (Er{sub 2}O{sub 3}) has many attractive properties. Monoclinic Er{sub 2}O{sub 3} has useful properties not found in stable cubic Er{sub 2}O{sub 3}, such as unique optical properties and high radiation damage tolerance. In this study, cubic Er{sub 2}O{sub 3} coating and Er{sub 2}O{sub 3} coating with mixed phases were prepared. The Raman scattering spectra of these coatings were investigated by using a confocal micro-Raman spectrometer equipped with 325, 473, 514, 532, 633, and 784 nm lasers. A total of 17 first-order Raman modes of monoclinic Er{sub 2}O{sub 3} were identified and assigned. The modes at 83, 112, 152, 170, 278, 290, 409, 446, 478, 521, 603, and 622 cm{sup −1} are of A{sub g} symmetry, whereas modes at 71, 98, 333, 409, 446, and 468 cm{sup −1} are of B{sub g} symmetry. This research provides basic data necessary for the characterization of monoclinic Er{sub 2}O{sub 3} by Raman spectroscopy.
- OSTI ID:
- 22258779
- Journal Information:
- Journal of Applied Physics, Vol. 114, Issue 19; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Proton states in the Z = 99 nucleus /sup 251/Es excited by /sup 251/Fm electron capture decay and /sup 250/Cf(. cap alpha. ,t) reaction
One- and three-quasiparticle states in /sup 249/Cf populated by the electron capture decay of 1. 70-h /sup 249/Es