Peak divergence in the curve of magnetoelectric coefficient versus dc bias magnetic field at resonance region for bi-layer magnetostrictive/piezoelectric composites
- Institute of Advanced Materials and Technology, University of Science and Technology Beijing, Beijing 100083 (China)
- Department of Physics, Zhejiang Normal University, Jinhua 321004, Zhejiang Province (China)
Magnetoelectric (ME) coefficient dependence on the bias magnetic field at resonance frequencies for the bi-layered bonded Terfenol-D/Pb(Zr,Ti)O{sub 3} composite was investigated. The resonance frequency decreases first and then increases with the bias magnetic field (H{sub DC}), showing a “V” shape in the range of 0 ∼ 5 kOe. Below the resonance frequency, the pattern of ME coefficient dependence on the H{sub DC} shows a single peak, but splits into a double-peak pattern when the testing frequency increases into a certain region. With increasing the frequency, a divergent evolution of the H{sub DC} patterns was observed. Domain motion and ΔE effect combined with magnetostriction-piezoelectric coupling effect were employed to explain this experimental result.
- OSTI ID:
- 22251730
- Journal Information:
- AIP Advances, Vol. 3, Issue 12; Other Information: (c) 2013 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetoelectric effect in piezoelectric/magnetostrictive multilayer (2-2) composites
Magnetoelectric effect in lead-free BNKLBT ceramic/terfenol-D continue fiber composite laminates